Mixed Metal Oxides of the Type CoxZn1-xFe2O4 as Photocatalysts for Malachite Green Degradation Under UV Light Irradiation

A combination of thermal and mechanical (high energy ball milling) treatment was applied in an attempt to obtain polycrystalline mixed metal binary and ternary oxides of the type CoxZn1-x Fe-2 O-4 (x = 0; 0.25; 0.5; 0.75; 1). The synthetic procedure used successfully produced single-phased, homogeneous ZnFe2 O-4, CoFe2 O-4, and Co-0.75 Zn-0.25 Fe-2 O-4, as well as mixed oxides, whose composition depended both on the duration of the high energy ball milling and the ratio Zn(II)/Co(II). The formation of spinel-like structures was proved by XRD, Mssbauer spectroscopy and Raman spectroscopy. For the characterization of the samples low-temperature N 2 adsorption, UV/Vis spectroscopy and transmission electron microscopy were applied. The energy band gap of the samples was calculated, suggesting they are promising photocatalysts. The decomposition of the Malachite Green in model water solutions under UV-light irradiation was successfully achieved in the presence of the samples as photocatalysts. The highest rate constant was obtained for the sample synthesized at longer milling time in combination with higher Zn( II)/Co( II) ratio. The photocatalytic activity of the ternary mixed oxides was compared with the pure hematite, alpha-Fe-2 O-3, and the binary ZnFe2 O-4 and CoFe2 O-4 ferrites with spinel structure that were treated in the same way. A synergetic effect of alpha-Fe-2 O-3 and the spinel-like structure on the photocatalytic properties of ternary mixed metal oxides was detected.