Fatigue-Life Prediction of Corroded Steel Bar Based on Fractal Theory

被引：7

作者：

Liu, Yang ^{[1
]}

Jiang, Nan ^{[1
]}

Zhang, Haiping ^{[1
]}

Li, Ming ^{[1
]}

机构：

[1] Changsha Univ Sci & Technol, Sch Civil Engn & Architecture, Key Lab Safety Control Bridge Engn, Minist Educ & Hunan Prov, Changsha 410114, Hunan, Peoples R China

来源：

JOURNAL OF MATERIALS IN CIVIL ENGINEERING | 2018年 / 30卷 / 09期

基金：

美国国家科学基金会;

关键词：

Steel bar; Fatigue life; Fractal characteristics; Three-dimensional (3D) surface morphology coefficient; PROBABILISTIC PREDICTION; REINFORCING BARS; RC BEAMS; CORROSION; BEHAVIOR; DEGRADATION; PERFORMANCE; STRENGTH;

D O I：

10.1061/(ASCE)MT.1943-5533.0002420

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This paper presents an experimental study that sought to characterize the effect of corrosion and fatigue load on the behavior of reinforcing steel bars. The surface profiles of corroded steel bars and the relationship between fatigue life and corrosion morphology were investigated. First, the corrosion process was accelerated by applying external direct current. Next, fatigue tests were performed on uncorroded specimens and precorroded specimens, and the results are presented and analyzed. A method for calculating the three-dimensional (3D) corrosion morphology coefficient of corroded steel bar is proposed. The fatigue life of corroded bars is significantly reduced because of corrosion morphology, and a logarithmic linear relationship exists between fatigue life and the corrosion morphology coefficient. Considering the corrosion morphology of corroded steel bars, a method is provided to calculate the fatigue life of a corroded steel bar based on the properties of uncorroded steel bar and the 3D surface morphology coefficient of corroded steel bars. The prediction results for corroded steel bars agree well with the experimental observations.

引用

页数：11

共 50 条

[1] Fatigue-Life Prediction Method Based on Small-Crack Theory in an Engine Material
Newman, James C., Jr.
Annigeri, Balkrishna S.
JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 2012, 134 (03):
[2] Study on fatigue properties and life prediction of corroded steel strands
Fan, Weijie
Zhou, Yuanzhen
Cheng, Pengju
Peng, Wei
JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2024, 217
[3] FATIGUE-LIFE PREDICTION METHOD BASED ON SMALL-CRACK THEORY IN AN ENGINE MATERIAL
Newman, James C., Jr.
Annigeri, Balkrishna S.
PROCEEDINGS OF THE ASME TURBO EXPO 2011, VOL 6, PTS A AND B, 2012, : 103 - 112
[4] Fatigue-life prediction methodology using small-crack theory
Newman, JC
Phillips, EP
Swain, MH
INTERNATIONAL JOURNAL OF FATIGUE, 1999, 21 (02) : 109 - 119
[5] Estimating the Effects of Corrosion Pitting Morphology on Residual Fatigue Properties of Corroded Steel Based on Fractal Theory
Ren, Songbo
Gu, Ying
Gao, Xinqiang
Gu, Song
Kong, Chao
Zeng, Shenghui
Liu, Peng
Li, Xiaoge
INTERNATIONAL JOURNAL OF STEEL STRUCTURES, 2023, 23 (02) : 480 - 492
[6] Estimating the Effects of Corrosion Pitting Morphology on Residual Fatigue Properties of Corroded Steel Based on Fractal Theory
Ren Songbo
Gu Ying
Gao Xinqiang
Gu Song
Kong Chao
Zeng Shenghui
Liu Peng
Li Xiaoge
International Journal of Steel Structures, 2023, 23 : 480 - 492
[7] FATIGUE-LIFE ENHANCEMENT OF STEEL BY NITROGEN IMPLANTATION
HU, WW
CLAYTON, CR
HERMAN, H
HIRVONEN, JK
KANT, RA
RADIATION EFFECTS AND DEFECTS IN SOLIDS, 1980, 49 (1-3): : 71 - 72
[8] Development of long fatigue-life steel for bearings
Doi, Kenji
Orihashi, Hideyuki
Matsushima, Yoshitake
Yasuki, Shinichi
Fukuzaki, Yoshio
Nakajima, Shinichi
R and D: Research and Development Kobe Steel Engineering Reports, 2000, 50 (01): : 49 - 52
[9] Fatigue-life calculations on pristine and corroded open-hole specimens using small-crack theory
Newman, J. C., Jr.
Abbott, W.
INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (8-9) : 1246 - 1253
[10] Approximate method for fatigue-life prediction of framed structures
Politecnico di Milano, Milano, Italy
Fatigue Fract Eng Mater Struct, 12 (1481-1491):

← 1 2 3 4 5 →