Complexity of deformation mechanism in neutron-irradiated 304L austenitic stainless steel at microstructural scale

The deformation mechanisms of neutron-irradiated 304 L stainless steel have been investigated using the in-situ electron backscattered diffraction (EBSD) technique. To decipher the role of irradiation, a detailed analysis was performed on irradiated miniature samples and compared with nonirradiated samples. At three levels of engineering strain, -0.0%, 4.8%, and 14.5%-microstructural features as well as EBSD were recorded at the identical location during in-situ deformation testing. Post-mortem analysis of the EBSD data revealed that the neutron-irradiated samples had higher fractions of the slip bands even at low amounts of deformation. Along with the slip bands, the neutron-irradiated sample showed the twins and martensitic phase formed almost parallel to the slip bands. In addition, the image results also indicated that the formation of twins and phases associated with the slip bands. A detailed mechanistic understanding has been investigated to identify the (111)gamma planes orientation with respect to the loading direction associated with the formation of twins and martensite. The newly formed deformation twins and martensite were also found to maintain this relationship when they existed together.