Magnetron sputtered hard a-C coatings of very high toughness

被引:76
|
作者
Zhang, S [1 ]
Bui, XL [1 ]
Fu, YQ [1 ]
机构
[1] Nanyang Technol Univ, Sch Mech & Prod Engn, Singapore 639798, Singapore
来源
SURFACE & COATINGS TECHNOLOGY | 2003年 / 167卷 / 2-3期
关键词
diamond-like carbon; tribology; adhesion strength; graphitization;
D O I
10.1016/S0257-8972(02)00900-3
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Hydrogen-free amorphous carbon coatings of high hardness (approximate to30 GPa) and toughness (plasticity from 50 to 60%) were deposited on 440C steel substrates by DC magnetron sputtering at target power density of 10.5 W/cm(2) in the bias range from 20 to - 150 V The surface topography, hardness and tribological behavior of the coatings were investigated. With the increase of bias voltage, coating hardness and surface smoothness increased at expense of some adhesion strength and an increase of coefficient of friction. All coatings showed low friction in humid air and graphitization was observed after a high number of rotation cycles. The graphitization adds more benefit aside from reducing friction: the graphite layer can considerably reduce the adhesive wear since it prevents the asperities of the two surfaces to be adhered to each other. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:137 / 142
页数:6
相关论文
共 50 条
  • [1] Raman and peels studies of magnetron sputtered a-C
    Zhang, S
    Jen, TM
    Zeng, XT
    Xie, H
    Hing, P
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2000, 14 (2-3): : 268 - 273
  • [2] Magnetron-sputtered nc-TiC/a-C(Al) tough nanocomposite coatings
    Zhang, S
    Bui, XL
    Fu, YQ
    THIN SOLID FILMS, 2004, 467 (1-2) : 261 - 266
  • [3] Investigation of the phase formation in magnetron sputtered hard multicomponent (HfNbTiVZr)C coatings
    Osinger, Barbara
    Mao, Huahai
    Fritze, Stefan
    Riekehr, Lars
    Jansson, Ulf
    Lewin, Erik
    MATERIALS & DESIGN, 2022, 221
  • [4] Magnetron sputtered nanocrystalline metastable (V,Al)(C,N) hard coatings
    Stueber, M.
    Ulrich, S.
    Leiste, H.
    Holleck, H.
    SURFACE & COATINGS TECHNOLOGY, 2011, 206 (04): : 610 - 616
  • [5] Raman spectroscopy measurements of DC-magnetron sputtered carbon nitride (a-C:N) thin films for magnetic hard disk coatings
    Neuhaeuser, M
    Hilgers, H
    Joeris, P
    White, R
    Windeln, J
    DIAMOND AND RELATED MATERIALS, 2000, 9 (08) : 1500 - 1505
  • [6] Investigation of toughness and wear resistance of a-C/a-C:Cr multilayer coatings
    Department of Mechanical Engineering, Chung-Hua University, Hsin Chu, 30067, Taiwan
    不详
    Key Eng Mat, 2007, (731-736): : 731 - 736
  • [7] Structure characterization and tribological study of magnetron sputtered nanocomposite nc-TiAlV(N,C)/a-C coatings
    Luo, Quanshun
    Wang, Shun Cai
    Zhou, Zhaoxia
    Chen, Linghao
    JOURNAL OF MATERIALS CHEMISTRY, 2011, 21 (26) : 9746 - 9756
  • [8] Toughness characteristics of arc enhanced magnetron sputtered SiCN hard films
    Wang, Y. F.
    Ma, S. L.
    Chu, P. K.
    SURFACE ENGINEERING, 2010, 26 (08) : 571 - 577
  • [9] Fracture toughness and sliding properties of magnetron sputtered CrBC and CrBCN coatings
    Wang, Qianzhi
    Zhou, Fei
    Ma, Qiang
    Callisti, Mauro
    Polcar, Tomas
    Yan, Jiwang
    APPLIED SURFACE SCIENCE, 2018, 443 : 635 - 643
  • [10] Preparation and characterisation of a-C and a-C:H coatings deposited by pulsed magnetron sputtering
    Czyzniewski, Andrzej
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (08): : 1027 - 1033