Magnetic properties and structure of FePt/FeMn multilayers

A systematic study of the magnetic properties by ion beam sputter-deposition system, was conducted in conjunction with the structure of FePt/FeMn multilayers fabricated onto MgO(0 0 1) substrates. Both parallel and perpendicular exchange biases were observed in the multilayers and were found to decrease drastically, as the deposition temperature is higher than 350 degrees C, which is evidently due to the interdiffusion at the interface. The thickness dependence study shows that the perpendicular magnetic anisotropy observed in the multilayers originates from surface anisotropy, being consistent with the decrease of perpendicular magnetic anisotropy as the deposition temperature is increased. The difference between parallel and perpendicular blocking temperatures that was clearly observed, is possibly due to the spin canting out of plane at the interface. (C) 2007 Elsevier B.V. All rights reserved.