The Influence of the Interface on Fracture Parameters

被引：1
|
作者：
Marsavina, L. [1 ]
Sadowski, T. [1 ]
机构：
[1] Lublin Univ Technol, Fac Civil & Sanit Engn, PL-20618 Lublin, Poland
来源：
DAMAGE AND FRACTURE MECHANICS: FAILURE ANALYSIS OF ENGINEERING MATERIALS AND STRUCTURES | 2009年
关键词：
Crack; Bi-Material Interface; Singularity Order; Stress Intensity Factor; LOADED CRACK; BIMATERIAL; PENETRATION;
D O I：
10.1007/978-90-481-2669-9_26
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The presence of cracks has a major impact on the reliability of advanced materials, like fiber or particle reinforced ceramic composites, and laminated ceramics. The understanding of the failure mechanisms is very important, as much as the estimation of fracture parameters at the tip of the crack approaching an interface. This paper presents the numerical results for singularity order, asymptotic stress field and fracture parameters for a crack ending on a bi-material ceramic interface. The effect of bi-axial loading on asymptotic stress field and stress intensity factors was investigated.
引用
收藏
页码：245 / 254
页数：10
相关论文
共 50 条
  • [1] Influence of the interface thickness on fracture parameters
    Leguillon, D
    COMPTES RENDUS DE L ACADEMIE DES SCIENCES SERIE II FASCICULE B-MECANIQUE PHYSIQUE CHIMIE ASTRONOMIE, 1996, 322 (07): : 533 - 539
  • [2] Elastodynamic parameters for dynamic interface fracture mechanics
    A. Noe
    K. P. Herrmann
    Acta Mechanica, 1997, 123 : 203 - 226
  • [3] FRACTURE PARAMETERS FOR THE ORTHOTROPIC BIMATERIAL INTERFACE CRACKS
    HWU, CB
    ENGINEERING FRACTURE MECHANICS, 1993, 45 (01) : 89 - 97
  • [4] Elastodynamic parameters for dynamic interface fracture mechanics
    Noe, A
    Herrmann, KP
    ACTA MECHANICA, 1997, 123 (1-4) : 203 - 226
  • [5] Effect of interface to strength and fracture parameters of RCC with cracks
    Zhang, Xiao-Gang
    Wang, Xue-Zhi
    Sun, Rong-Shu
    Huang, Zhi-Qiang
    Shenzhen Daxue Xuebao (Ligong Ban)/Journal of Shenzhen University Science and Engineering, 2007, 24 (03): : 240 - 245
  • [6] NUMERICAL EVALUATION OF INTERFACE FRACTURE PARAMETERS USING ADINA
    LEE, KM
    BUYUKOZTURK, O
    LEUNG, CKY
    COMPUTERS & STRUCTURES, 1993, 47 (4-5) : 547 - 552
  • [7] EFFECT OF INTERFACE GEOMETRY ON FRACTURE PARAMETERS AT CORRUGATED INTERFACES
    Desyatova, Anastasia S.
    Dzenis, Yuris A.
    IMECE 2009: PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, VOL 11, 2010, : 219 - 220
  • [8] Effect of Elastic and Link Interface on Fracture Parameters of Nanocomposites
    Mahdiye Hamedi
    Fibers and Polymers, 2022, 23 : 3493 - 3504
  • [9] A polling direction influence on fracture parameters of a limited permeable interface crack in a piezoelectric bi-material
    Viun, O.
    Komarov, A.
    Lapusta, Y.
    Loboda, V.
    ENGINEERING FRACTURE MECHANICS, 2018, 191 : 143 - 152
  • [10] Two Objective and Independent Fracture Parameters for Interface Cracks
    Zhao, Jia-Min
    Wang, He-Ling
    Liu, Bin
    JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 2017, 84 (04):
12345