Fracture characteristics of thermally exposed 9Cr-1Mo steel after tensile and impact testing at room temperature

被引：60
|
作者：
Blach, Juraj [1 ]
Falat, Ladislav [1 ]
Sevc, Peter [1 ]
机构：
[1] Slovak Acad Sci, Inst Mat Res, Kosice 04001, Slovakia
来源：
ENGINEERING FAILURE ANALYSIS | 2009年 / 16卷 / 05期
关键词：
9Cr-1Mo steel; Thermal exposition; Microstructure; Tensile and impact properties; Fracture mode; MECHANICAL-PROPERTIES; DUCTILITY;
D O I：
10.1016/j.engfailanal.2008.09.003
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The paper deals with the fracture analysis of thermally exposed 9Cr-1Mo ferritic steel after tensile and impact testing at room temperature. The temperatures of the thermal expositions were 580, 620, and 650 degrees C, respectively. The duration of annealing experiments varied from 500 to 5000 h. The influence of thermal expositions on Vickers hardness as well as tensile properties was found to be negligible. On the other hand, remarkable effects of the annealing on room temperature impact toughness were observed. Fracture behaviour of the 9Cr-1Mo steel is strongly affected by the presence of precipitates of secondary phases. Fracture surfaces of tensile samples indicate mainly transgranular dimple fracture mechanism. By contrast, the fracture mode of the samples after impact testing is more complex. It shows both - ductile dimple tearing as well as inter-lath decohesion. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1397 / 1403
页数：7
相关论文
共 50 条
  • [1] CREEP FRACTURE OF A 9CR-1MO STEEL
    BARKER, E
    LLOYD, GJ
    PILKINGTON, R
    MATERIALS SCIENCE AND ENGINEERING, 1986, 84 (1-2): : 49 - 64
  • [2] Ratcheting Fatigue Behavior of Modified 9Cr-1Mo Steel at Room Temperature
    Mishra, Prerna
    Rajpurohit, R. S.
    Srinivas, N. C. Santhi
    Sastry, G. V. S.
    Singh, Vakil
    METALS AND MATERIALS INTERNATIONAL, 2021, 27 (12) : 4922 - 4936
  • [3] Effect of test temperature on fracture toughness of modified 9Cr-1Mo steel
    Dutt, B. Shashank
    Babu, M. Nani
    Venugopal, S.
    Sasikala, G.
    Bhaduri, A. K.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (10) : 1527 - 1533
  • [4] High temperature tensile testing of modified 9Cr-1Mo after irradiation with high energy protons
    Toloczko, MB
    Hamilton, ML
    Maloy, SA
    JOURNAL OF NUCLEAR MATERIALS, 2003, 318 : 200 - 206
  • [5] Compatibility of 9Cr-1Mo steel exposed to thermally convective Pb-17Li
    Chakraborty, P. (myworld.pc@gmail.com), 2013, Elsevier Editora Ltda (02)
  • [6] Influence of strain rate and temperature on tensile properties of 9Cr-1Mo ferritic steel
    Choudhary, B. K.
    Srinivasan, V. S.
    Mathew, M. D.
    MATERIALS AT HIGH TEMPERATURES, 2011, 28 (02) : 155 - 161
  • [7] Influence of temperature on tensile flow and workhardening behaviour of modified 9Cr-1Mo steel
    Sakthivel, T.
    Laha, K.
    Nandagopal, M.
    Mathew, M. D.
    MATERIALS AT HIGH TEMPERATURES, 2014, 31 (01) : 60 - 68
  • [8] Characterization of a precrept modified 9Cr-1Mo steel through room temperature tensile and strain rate change tests
    Dwivedi, VS
    Jha, BK
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (02): : 221 - 230
  • [9] Low cycle fatigue behavior of modified 9Cr-1Mo steel at room temperature
    Verma, Preeti
    Srinivas, N. C. Santhi
    Singh, S. R.
    Singh, Vakil
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 652 : 30 - 41
  • [10] Fracture toughness of irradiated modified 9Cr-1Mo steel
    Kim, Sung Ho
    Yoon, Ji-Hyun
    Ryu, Woo Seog
    Lee, Chan Bock
    Hong, Jun Hwa
    JOURNAL OF NUCLEAR MATERIALS, 2009, 386-88 : 387 - 389
12345