Effect of casting defect on mechanical properties of 17-4PH stainless steel

Damage and integrity evaluation techniques should be developed steadily in order to ensure the reliability and the economic efficiency of gas turbine engines. Casting defects may exist in most casting components of gas turbine engines, and the defects could give serious effect on mechanical properties and fracture toughness. Therefore, it is very important to understand the effect of casting defects on the above properties in order to predict the safety and life of components. In this study, specimens with internal casting defects, made from 17-4PH stainless steel, were prepared and evaluated and characterized based on the volume fraction of defects. The relation between mechanical properties such as tensile, low cycle fatigue and fracture toughness and volume fraction of defect has been investigated. As a result of the analysis, the mechanical properties of 17-4PH decreased as the defect volume fraction increased with very good linearity. The mechanical properties also showed an inversely proportional relationship to electrical resistivity.