Effect of Alumina on Liquid Phase Formation in Sintering Process of Iron Ore Fines

被引:12
|
作者
Guo, Hui [1 ]
Guo, Xing-Min [1 ]
机构
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, 30 Xueyuan Rd, Beijing 100083, Peoples R China
基金
中国国家自然科学基金;
关键词
alumina; calcium ferrites; liquid phase; sinter; SILICO-FERRITE; CALCIUM; SYSTEM; BEHAVIOR; OXIDE; AIR; ASSIMILATION; HEMATITE; FURNACE; AL2O3;
D O I
10.1002/srin.201900138
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The formation of liquid phase is of great significance for improving the quality of high basicity sinter which is widely used as raw materials in blast furnace ironmaking. As an important component of gangue in iron ore, alumina affects the amount of liquid phase by influencing the formation of calcium ferrites-bonding phase. In this work, the hematite solid solution with aluminum (H-ss) was prepared and sintered with CaO to investigate the effect of alumina on liquid phase formation in sintering process of iron ore fines. Three homogeneous phases of CaFe2O4 (CF), Ca2Fe15.57O25.56 (CF3.9), and Ca3.18Fe15.48Al1.34O28 (CFA) are prepared to determine the melting temperature by using DSC method. XRD, SEM-EDS, and optical microscope are used to characterize the change of mineral and microstructure of sintered samples. The results show that an Fe-rich calcium ferrite CF3.9 is produced above 1200 degrees C in Fe2O3-CaO binary system. The liquid phase formation temperature can be reduced to 1206 degrees C when CF3.9 and CF coexist. The ternary calcium ferrite CFA, which has a eutectic temperature of 1201 degrees C with CF, is generated above 990 degrees C in Fe2O3-CaO-Al2O3 ternary system. The formation of liquid phase is promoted by adding alumina in moderation through changing the mass ratio of CF to CFA, and the largest amount of liquid phase is produced when the ratio is 8:2.
引用
收藏
页数:9
相关论文
共 50 条
  • [1] Effect of BaSO4 on phase composition and sintering process of iron ore fines
    Jian-tao Ju
    Chen-mei Tang
    Guang-heng Ji
    Xiang-dong Xing
    Gui-qing Zhao
    Xin-tai Jiang
    Feng-lin Lu
    [J]. Journal of Iron and Steel Research International, 2022, 29 : 408 - 417
  • [2] Effect of BaSO4 on phase composition and sintering process of iron ore fines
    Ju, Jian-tao
    Tang, Chen-mei
    Ji, Guang-heng
    Xing, Xiang-dong
    Zhao, Gui-qing
    Jiang, Xin-tai
    Lu, Feng-lin
    [J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2022, 29 (03) : 408 - 417
  • [3] Effect of Thermodynamic Melt Formation Characteristics on Liquid Phase Fluidity of Iron Ore in the Sintering Process
    Wu, Shengli
    Li, Heping
    Zhang, Weili
    Su, Bo
    [J]. METALS, 2019, 9 (04):
  • [4] Effect of aluminum occurrence state on the formation of calcium ferrites in the sintering process of iron ore fines
    Guo, Hui
    Guo, Xing-Min
    [J]. Iron and Steel Technology, 2019, 16 (06): : 162 - 172
  • [5] Utilization of Pellet Fines in the Iron Ore Sintering Process
    Dhanraj Patil
    Akhil Singh
    Vinayak Bhosekar
    Nageswar Rao
    C. B. Dayanand
    Rameshwar Sah
    [J]. Transactions of the Indian Institute of Metals, 2023, 76 : 2985 - 2992
  • [6] Utilization of Pellet Fines in the Iron Ore Sintering Process
    Patil, Dhanraj
    Singh, Akhil
    Bhosekar, Vinayak
    Rao, Nageswar
    Dayanand, C. B.
    Sah, Rameshwar
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2023, 76 (11) : 2985 - 2992
  • [7] CHARACTERISTICS OF IRON-ORE FINES FOR SINTERING
    HARUNA, J
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (12): : S819 - S819
  • [8] Effect of ore types on high temperature sintering characteristics of iron ore fines and concentrate
    Han, Hongliang
    Lu, Liming
    Hapugoda, Sarath
    [J]. MINERALS ENGINEERING, 2023, 197
  • [9] Effect of alumina on slag-metal separation during iron nugget formation from high alumina Indian iron ore fines
    Borra, C. R.
    Dwarapudi, S.
    Kapure, G.
    Tathavadkar, V.
    Denys, M. B.
    [J]. IRONMAKING & STEELMAKING, 2013, 40 (06) : 443 - 451
  • [10] A forecast model of the sinter tumble strength in iron ore fines sintering process
    Gao, Qiangjian
    Wang, Hui
    Pan, Xiangyang
    Jiang, Xin
    Zheng, Haiyan
    Shen, Fengman
    [J]. POWDER TECHNOLOGY, 2021, 390 : 256 - 267