Relationship between nanoleakage and microtensile bond strength at the resin-dentin interface

To evaluate the correlation between microtensile dentin bond strength (muTBS) and silver ion penetration, two total-etch 3-step and one self-etch 2-step system were investigated. OptiBond FL adhesive was applied to flat occlusal dentin on six non-carious human molars, and a resin composite "crown" was formed in 2 mm increments. After 24-hour water storage, the teeth were sectioned with a low-speed diamond saw to obtain four-square sticks (similar to2 nun X 2 nun) per tooth. Cylindrical tensile test specimens were formed with an 0.5 mm(2) cross-sectional area. Nail varnish was applied to the dentin within 0.5-1.0 mm of the interface before immersing in 50% silver nitrate for 15 minutes. Following silver fixation, tensile testing was performed in a Zwick UTM at 1 mm/minute using a passive gripping fixture to obtain 72-hour muTBS [23.9 MPa]. The percentage area of silver penetration was measured on debonded specimens using light microscopy and Image-Pro Plus Software [89%]. The procedures were repeated using Scotchbond Multi-Purpose Plus [muTBS =27.8 MPa; nanoleakage = 67%] and Clearfil SE bond [muTBS = 36 MPa; nanoleakage = 55%]. No significant correlation between microtensile bond strength and nanoleakage was found for all systems. A weak-to-moderate negative relationship was found between muTBS and nanoleakage for OptiBond FL (Spearman r = -0.3844). No correlation was found for the remaining adhesive systems. The correlation between these two common laboratory measurements appears to be adhesive-system dependent.