Study of physical properties of cobalt substituted Pr0.7Ca0.3MnO3 ceramics

An investigation on single phase semiconducting polycrystalline Pr0.7Ca0.3MnO3 and Pr0.7Ca0.3MnCo0.1O3 crystallized in the orthorhombic system with Prima space group is reported. We found that sigma(DC) increases when introducing Co for T < 110 K but for T > 110 K, it decreases. Also, the contribution of hopping process in conduction mechanism was in agreement with the Jonscher law and Mott theory. Capacitance was extensively dependent on temperature and frequency. A dielectric transition was observed at T=150 K for the doped compound. The temperature dependence of dielectric permittivity is well described by Curie Weiss law. The parameter of deviation from Curie Weiss behavior to modified Curie Weiss law is found to be Delta T-m=30 K. The substitution of Mn by Co was found to destroy the charge order state observed in the parent compound and to induce a ferromagnetic phase at low temperature. The cobalt-substituted sample exhibits a maximum value of magnetic entropy change vertical bar Delta S-max vertical bar=3.2 J kg(-1) K-1 land a large relative cooling power with a maximum value of 301 J/kg under an applied field of 5 T. Technically, these large values make the prepared material very promising for magnetic refrigeration. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.