HDPE/LLDPE reactor blends with bimodal microstructures - Part II: rheological properties

Reactor blends of polyethylene/poly(ethylene-co-1-octene) resins with bimodal molecular weight and bimodal short chain branching distributions were synthesized in a two-step polymerization process. The compositions of these blends range from low molecular weight (LMW) homopolymer to high molecular weight (HMW) copolymer and vice versa HMW homopolymer to LMW copolymer. The shear flow characteristics of these polymers in the typical processing range mostly depend on the molecular weight and MWD of the polymer and are independent of the short chain branch content. From oscillatory shear measurements, it was observed that the viscosity of HMW polymers was reduced with the addition of LMW material. For the polymers produced with this two-step polymerization process, the LMW homopolymer and HMW copolymer blends and HMW homopolymer and LMW copolymer blends were melt miscible, despite the large viscosity differences of the pure components. (C) 2002 Elsevier Science Ltd. All rights reserved.