The effect of yttrium content on the oxidation-induced degradation of NiCoCrAlY coatings and the influence of surface roughness on the oxidation of NiCoCrAlY and platinum aluminide coatings

被引：3
|
作者：
Yanar, N. M. [1 ]
Meier, E. M. [1 ]
Pettit, F. S. [1 ]
Meier, G. H. [1 ]
机构：
[1] Univ Pittsburgh, Dept Mech Engn & Mat Sci, Pittsburgh, PA 15261 USA
来源：
MATERIALS AT HIGH TEMPERATURES | 2009年 / 26卷 / 03期
关键词：
yttrium; NiCoCrAlY coatings; platinum aluminide coatings; cyclic oxidation; surface roughness; INSTABILITY; BEHAVIOR; FAILURE;
D O I：
10.3184/096034009X472231
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
It has been found that the yttrium content of NiCoCrAlY coatings affects the useful lives of such coatings during cyclic oxidation. In particular, NiCoCrAlY coatings with 0.1wt% yttrium have more than twice the lifetime at 1100 degrees C compared to NiCoCrAlY coatings with 0.5wt% yttrium. The mechanism by which the yttrium concentration influences the degradation of NiCoCrAlY coatings will be described. It has also been observed that the adverse effect of yttrium can be inhibited by reducing the roughness of the coating surface. The influence of surface condition on the oxidation of yttrium in NiCoCrAlY coatings will be examined in detail and the effects of surface roughness on the oxidation of NiCoCrAlY and platinum aluminide coatings will be compared. Finally the effects of yttrium in the substrate alloy on the oxidation of platinum aluminide coatings will be discussed.
引用
收藏
页码：331 / 338
页数：8
相关论文
共 50 条
  • [1] Oxidation protection of NiCoCrAlY coatings on γ-TiAl
    Wang, QM
    Guo, MH
    Ke, PL
    Gong, J
    Sun, C
    Wen, LS
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 (02) : 423 - 426
  • [2] Oxidation protection of NiCoCrAlY coatings on γ-TiAl
    王启民
    郭明虎
    柯培玲
    宫骏
    孙超
    闻立时
    TransactionsofNonferrousMetalsSocietyofChina, 2005, (02) : 423 - 426
  • [3] Influence of superalloy substrate roughness on adhesion and oxidation behavior of magnetron-sputtered NiCoCrAlY coatings
    Li, Zhiming
    Qian, Shiqiang
    Wang, Wei
    APPLIED SURFACE SCIENCE, 2011, 257 (24) : 10414 - 10420
  • [4] Effect of surface preparation on the durability of NiCoCrAlY coatings for oxidation protection and bond coats for thermal barrier coatings
    Jackson, E. M. Meier
    Yanar, N. M.
    Maris-Jakubowski, M. C.
    Onal-Hance, K.
    Meier, G. H.
    Pettit, F. S.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2008, 59 (06): : 494 - 500
  • [5] Thermal stability and oxidation behavior of nanostructured NiCoCrAlY coatings
    Mercier, Dominic
    Gauntt, Bryan D.
    Brochu, Mathieu
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 (17-18): : 4162 - 4168
  • [6] On the initiation of cyclic oxidation-induced rumpling of platinum-modified nickel aluminide coatings
    Dryepondt, Sebastien
    Porter, John R.
    Clarke, David R.
    ACTA MATERIALIA, 2009, 57 (06) : 1717 - 1723
  • [7] Cyclic oxidation-induced cracking of platinum-modified nickel-aluminide coatings
    Dryepondt, Sebastien
    Clarke, David R.
    SCRIPTA MATERIALIA, 2009, 60 (10) : 917 - 920
  • [8] Effects of surface finish on the initial oxidation of HVAF-sprayed NiCoCrAlY coatings
    Zhang, Pimin
    Sadeghimeresht, Esmaeil
    Chen, Shula
    Li, Xin-Hai
    Markocsan, Nicolaie
    Joshi, Shrikant
    Chen, Weimin
    Buyanova, Irina A.
    Peng, Ru Lin
    SURFACE & COATINGS TECHNOLOGY, 2019, 364 : 43 - 56
  • [9] Effect of vacuum annealing on initial oxidation behavior and alumina transition of NiCoCrAlY coatings
    Ullah, A.
    Khan, A.
    Bao, Z. B.
    Yu, C. T.
    Zhu, S. L.
    Wang, F. H.
    SURFACE & COATINGS TECHNOLOGY, 2020, 404
  • [10] Comparative Study of the cyclic oxidation resistance of NiCrAlY and NiCoCrAlY coatings
    Liu, Jianming
    Yu, Yueguang
    Ren, Xianjing
    Zhang, Deming
    Shen, Jie
    ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3, 2013, 652-654 : 1810 - +
12345