Premature water-slide corrosion of furnace wall tubes in a high-pressure boiler

被引：0
|
作者：
Mobin, A.
Malik, A. U.
Andijani, I. N.
Al-Muaili, F.
Al-Hajri, M.
机构：
[1] SWCC, Saline Water Desalinat Res Inst, Al Jubail 31951, Saudi Arabia
[2] Aligarh Muslim Univ, Fac Engn & Technol, Aligarh, Uttar Pradesh, India
来源：
MATERIALS PERFORMANCE | 2006年 / 45卷 / 09期
关键词：
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This article describes the results of an investigation into the premature water-side corrosion of furnance wall tubes of a high-pressure boiler. After similar to 13,869 h of operation, an unscheduled inspection of the internal condition of the furnace wall tubes revealed considerable corrosion, which was quite significant in view of the short service life of the boiler. The cause of corrosion was determined by on-site visual inspection of the boiler and detailed macro- and micro-examinations of inner scales on the tubes. To prevent serious metal loss from corrosion, corrective measures were recommended.
引用
收藏
页码：44 / 49
页数：6
相关论文
共 50 条
  • [1] Substantiation of causes for damage of water-wall tubes of an external salt compartment of a high-pressure boiler
    Fedorov A.I.
    Thermal Engineering, 2014, 61 (10) : 724 - 730
  • [2] Failure avoidance -: Phosphate attack as caustic corrosion in high-pressure boiler tubes
    de Romero, MF
    Pérez, O
    Navarro, A
    MATERIALS PERFORMANCE, 1999, 38 (03) : 72 - 75
  • [3] Caustic corrosion failure of back wall riser tube in a high-pressure boiler
    Mobin M.
    Malik A.U.
    Journal of Failure Analysis and Prevention, 2011, 11 (4) : 357 - 362
  • [4] HYDROGEN ATTACK ON WATERWALL TUBES IN A HIGH-PRESSURE BOILER
    HENDRIX, DE
    MATERIALS PERFORMANCE, 1995, 34 (08) : 46 - 51
  • [5] Investigations on the failure of economizer tubes in a high-pressure boiler
    Mobin M.
    Malik A.U.
    Al-Hajri M.
    Journal of Failure Analysis and Prevention, 2008, 8 (1) : 69 - 74
  • [6] Corrosion fatigue damage evaluation of boiler water-wall tubes
    Ishikawajima Harima Giho, 4 (256-261):
  • [7] Investigation on high temperature corrosion of water-cooled wall tubes at a 300 MW boiler
    Xiong, Xiaohe
    Liu, Xing
    Tan, Houzhang
    Deng, Shuanghui
    JOURNAL OF THE ENERGY INSTITUTE, 2020, 93 (01) : 377 - 386
  • [8] METALLOGRAPHIC DAMAGE ANALYSIS AT EVAPORATOR TUBES OF A HIGH-PRESSURE BOILER
    ZOLNAY, G
    NEUE HUTTE, 1984, 29 (05): : 189 - 189
  • [9] Analysis of high temperature corrosion and wear damage on furnace water wall in pulverized coal firing boiler
    Kyo S.
    Nakamori M.
    Kurokawa K.
    Narita T.
    Zairyo to Kankyo/ Corrosion Engineering, 2010, 59 (12): : 456 - 463
  • [10] High-pressure thin-wall drift tubes
    V. I. Davkov
    K. I. Davkov
    V. V. Myalkovskiy
    V. D. Peshekhonov
    Instruments and Experimental Techniques, 2008, 51 : 787 - 791
12345