Warm deep drawing of wrought magnesium alloy sheets produced by semi-solid roll strip-casting process

This paper is concerned with the development of a continuous strip-casting technology to facilitate the manufacture of magnesium sheet alloys economically whilst maintaining high quality. Established in the paper is warm formability of cast magnesium alloy sheets after being hot rolled by semi-solid roll strip-casting process. It has been found that magnesium sheet with 2.0-4.0 mm thickness could be produced at a speed of 25 m/min. Hot rolling and annealing temperatures during hot rolling were also changed to examine which condition would be appropriate for producing wrought magnesium alloys with good formability. Microstructures of the crystals of the manufactured wrought magnesium alloys were observed. It has been found that a limiting drawing ratio of 2.7 was possible in a warm deep-drawing test of the cast magnesium alloy sheets after being hot rolled. (c) 2006 Elsevier Ltd. All rights reserved.