Crack formation mechanisms in Al2O3/Kovar brazed joint

被引：6
|
作者：
Yu, Z. S. [1 ]
Yang, P. [1 ]
Li, R. F. [1 ]
Qi, K. [1 ]
机构：
[1] Shanghai Univ Engn Sci, Coll Mat Engn, Shanghai 200336, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2006年 / 22卷 / 07期
关键词：
Al2O3; ceramic; brazing; crack; Ti-Cu-Ni filler metal; intermetallic compound;
D O I：
10.1179/174328406X102435
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Joining of metal to ceramic is difficult owing to the formation of cracks at the interface of brazed joint. In the present paper, the crack forming metallurgical mechanisms is studied primarily. The vacuum brazing experiments of ceramic Al2O3 and Kovar, Ni, Fe or Co metals are all conducted. It can be obtained that the cracks could be formed at the Al2O3-Kovar and Al2O3-Fe joint, but not at the Al2O3-Ni and Al2O3-Co joint. In addition, the interfacial morphology and compound composition near cracks are confirmed. It can be concluded that the formation of intermetallic compound FexTiy is the main reason why cracks formed.
引用
收藏
页码：864 / 866
页数：3
相关论文
共 50 条
  • [1] Effects of mo interlayer on suppressing cracks in Al2O3/Kovar brazed joint
    Shanghai University of Engineering Science, Shanghai 200336, China
    Xiyou Jinshu Cailiao Yu Gongcheng, 2008, 12 (2118-2121):
  • [2] Effects of Mo Interlayer on Suppressing Cracks in Al2O3/Kovar Brazed Joint
    Yu Zhishui
    Yang Pei
    Qi Kai
    Li Ruifeng
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (12) : 2118 - 2121
  • [3] Role of Ti diffusion on the formation of phases in the Al2O3–Al2O3 brazed interface
    Abhijit Kar
    Sudipta Mandal
    Rabindra N. Ghosh
    Tamal K. Ghosh
    Ajoy Kumar Ray
    Journal of Materials Science, 2007, 42 : 5556 - 5561
  • [4] Effects of Cu interlayers on the microstructure and mechanical properties of Al2O3/AgCuTi/Kovar brazed joints
    Wang, Ying
    Jin, Chenkai
    Yang, Zhenwen
    Wang, Dongpo
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2019, 16 (03) : 896 - 906
  • [5] Microstructure of the Al2O3/Al2O3 joint brazed with Cu-Zn-Ti filler metal
    Fang, HY
    Yang, JG
    Yu, XY
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2001, 17 : S186 - S188
  • [6] Microstructure of the Al2O3/Al2O3 joint brazed with Cu-Zn-Ti filler metal
    Fang, Hongyuan
    Yang, Jianguo
    Yu, Xiuyu
    Journal of Materials Science and Technology, 2001, 17 (SUPPL.):
  • [7] Interfacial structure and mechanical property of Al2O3 and Invar brazed joint
    赵磊
    侯金保
    李晓红
    China Welding, 2016, 25 (04) : 68 - 73
  • [8] Air-brazed Al2O3 joint with a novel bismuth glass
    Guo, Wei
    Fu, Li
    He, Peng
    Lin, Tiesong
    Wan, Meiling
    Hou, Jing
    Wu, Yahui
    Liu, Xiaochao
    Shen, Zhikang
    CERAMICS INTERNATIONAL, 2019, 45 (12) : 15213 - 15222
  • [9] Al2O3/Al2O3 joint brazed with Al2O3-particulate-contained composite Ag-Cu-Ti filler material
    Yang, JG
    Fang, HY
    Wan, X
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2005, 21 (05) : 782 - 784
  • [10] Al2O3/Al2O3 Joint Brazed with Al2O3-particulate-contained Composite Ag-Cu-Ti Filler Material
    Jianguo YANG Hongyuan FANG and Xin WANState Key Laboratory of Advanced Welding Production Technology
    Journal of Materials Science & Technology, 2005, (05) : 176 - 178
12345