High-performance zero-bias ultraviolet photodetector based on p-GaN/n-ZnO heterojunction

Lattice-match p-GaN and n-ZnO bilayers were heteroepitaxially grown on the c-sapphire substrate by metal organic chemical vapor deposition and molecular beam epitaxy technique, respectively. X-ray diffraction and photoluminescence investigations revealed the high crystal quality of the bilayer films. Subsequently, a p-GaN/n-ZnO heterojunction photodetector was fabricated. The p-n junction exhibited a clear rectifying I-V characteristic with a turn-on voltage of 3.7 V. At zero-bias voltage, the peak responsivity was 0.68 mA/W at 358 nm, which is one of the best performances reported for p-GaN/n-ZnO heterojunction detectors due to the excellent crystal quality of the bilayer films. These show that the high-performance p-GaN/n-ZnO heterojunction diode is potential for applications of portable UV detectors without driving power. (C) 2014 AIP Publishing LLC.