Relative humidity and deterioration of concrete under freeze-thaw load

被引：40
|
作者：
Wang, Zhendi [1 ]
Zeng, Qiang [2 ]
Wu, Yuekai [3 ]
Wang, Ling [1 ]
Yao, Yan [1 ]
Li, Kefei [2 ]
机构：
[1] China Bldg Mat Acad, State Key Lab Green Bldg Mat, Beijing 100024, Peoples R China
[2] Tsinghua Univ, Inst Bldg Mat, Dept Civil Engn, Beijing 100084, PR, Peoples R China
[3] Beijing Univ Civil Engn & Architecture, Beijing 100044, PR, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2014年 / 62卷
基金：
中国博士后科学基金; 中国国家自然科学基金;
关键词：
Relative humidity; Deterioration; Concrete; Freeze-thaw; INTERNAL FROST DAMAGE; POROUS MATERIALS; CEMENT; BEHAVIOR; PHASE; HYSTERESIS; SURFACE; MODEL; WATER; PASTE;
D O I：
10.1016/j.conbuildmat.2014.03.027
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Evolution of internal relative humidity (RH) and deterioration of concrete under cyclic freeze-thaw (F-T) load were studied. RH values of concrete specimens were monitored upon freezing and thawing. Compressive strength, mass loss, visual ratings and porosimetry were used to evaluate changes in concrete. Decreasing water to cement ratio (w/c) decreased the steady-state internal RH. RH-temperature curves showed that freezing temperature was independent of F-T cycles, while thawing temperature varied with F-T cycle and w/c. More severe deterioration, but less alteration of pore structure, occurred in higher w/c concrete - increasing w/c increased ice formation in pores, and thus effective crystallization pressure and liquid pressure. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：18 / 27
页数：10
相关论文
共 50 条
  • [1] Deterioration mechanism of coal gangue concrete under the coupling action of bending load and freeze-thaw
    Xiao, Guan
    Yang, Gao
    Jixi, Chen
    Ruyi, Zhang
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 338
  • [2] INFLUENCE OF SALT ON FREEZE-THAW DETERIORATION OF CONCRETE
    CANTOR, TR
    KNEETER, CP
    MATERIALS PERFORMANCE, 1977, 16 (05) : 28 - 32
  • [3] Solutions for freeze-thaw deterioration of concrete dams
    Harlan, RC
    Onken, SC
    ASSOCIATION OF STATE DAM SAFETY OFFICIALS 1998 ANNUAL CONFERENCE PROCEEDINGS, 1998, : 895 - 906
  • [4] Deterioration Mechanism of Sulfate Attack on Concrete under Freeze-thaw Cycles
    NIU Ditao
    JIANG Lei
    FEI Qiannan
    Journal of Wuhan University of Technology(Materials Science Edition), 2013, 28 (06) : 1172 - 1176
  • [5] Deterioration Mechanism of Sulfate Attack on Concrete under Freeze-thaw Cycles
    Niu Ditao
    Jiang Lei
    Fei Qiannan
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2013, 28 (06): : 1172 - 1176
  • [6] Deterioration mechanism of sulfate attack on concrete under freeze-thaw cycles
    Ditao Niu
    Lei Jiang
    Qiannan Fei
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2013, 28 : 1172 - 1176
  • [7] On Deterioration Mechanism of Concrete Exposed to Freeze-Thaw Cycles
    Trofimov, B. Ya
    Kramar, L. Ya
    Schuldyakov, K. V.
    INTERNATIONAL CONFERENCE ON CONSTRUCTION, ARCHITECTURE AND TECHNOSPHERE SAFETY (ICCATS 2017), 2017, 262
  • [8] INFLUENCE OF SALT ON FREEZE-THAW DETERIORATION OF CONCRETE - REPLY
    CANTOR, TR
    KNEETER, CP
    MATERIALS PERFORMANCE, 1977, 16 (10) : 43 - 43
  • [9] Methods of mitigation of freeze-thaw deterioration of aging concrete dams
    Onken, SC
    Harlan, RC
    DEALING WITH AGING DAMS, 1999, : 495 - 507
  • [10] Experimental Study on Deterioration Characteristics of Prestressed Concrete under the Coupling of Freeze-Thaw and Corrosion
    Cui, Wei
    Liu, Manman
    Wang, Lixin
    Guan, Wei
    Song, Huifang
    Li, Feng
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2022, 34 (02)
12345