A comparison between gravimetric and volumetric techniques of wear measurement of UHMWPE acetabular cups against zirconia and cobalt-chromium-molybdenum femoral heads in a hip simulator

Five cobalt-chromium-molybdenum (CoCrMo) and five zirconia femoral head components have been wear tested against 28 mm diameter ultra high molecular weight polyethylene (UHMWPE) acetabular cups for 5 million cycles in the Durham hip joint wear simulator using bovine serum as a lubricant. Wear measurements used gravimetric and volumetric techniques and no statistically significant difference was found between the measurement methods. The wear rates of the acetabular cups against both femoral heads are presented for both measurement methods. The UHMWPE acetabular cups showed a statistically significant higher linear wear rate for the first 2 million cycles than the lower linear wear rate from 2 million cycles to the end of the test, against both femoral head materials. Over the full duration of the wear test, the wear rates of acetabular cups articulating against zirconia femoral heads were lower than against CoCrMo femoral heads. The wear rates up to 2 million cycles and from 2 to 5 million cycles for both femoral head materials were consistent with other studies.