Post-oxidizing effects on surface characteristics of salt bath nitrocarburized AISI 02 tool steel type

The effect of post-oxidizing treatment on the characteristics of modified surface layers produced by salt bath nitrocarburizing on the industrial American Iron and Steel Institute (AISI) 02 tool steel types is investigated. Nitrocarburizing treatment is performed for 6 h and 8 h at 570 degrees C and post-oxidizing treatment for 30, 60 and 90 min at 520 degrees C, using argon-steam mixture. Formed layers are characterized by their basic properties such as thickness layer, depth, surface hardness and wear resistance. Detailed estimation of the modified metal surface quality, in terms of chemical composition, formed phases, microstructures and diffusion mechanisms are performed by metallographic techniques, EDX, X-ray diffraction, scanning electron microscopy (SEM) and glow discharge optical electron spectroscopy (GDOES). The corrosion resistance was investigated in 0.4 m H2SO4 solutions, using steady-state electrochemical polarization methods. The obtained results revealed the existence of a superficial oxide layer which consists of magnetite (Fe3O4) and hematite (Fe2O3) and the presence of an e-phase associated with a small amount of gamma'-phase. Important improvements in wear, microhardness and corrosion resistance occur after these treatments and it is specifically concluded that the sole application of a nitrocarburizing treatment does not significantly ameliorate the corrosion resistance of the as-received steel. In fact, post-oxidation treatment contributes to increase corrosion resistance by forming a dense magnetite layer and at the same time, it partially covers the compound layer pores. Copyright (C) 2009 John Wiley & Sons, Ltd.