Nanostructured red-emitting MgGa2O4:Eu3+ phosphors

Nano-grained phosphors of Eu3+-doped MgGa2O4 crystallites were prepared by sol-gel technique. The characterization and optical properties of luminescent MgGa2O4:Eu3+ powders have been investigated. The dried sol-gel powders were calcined in air at different temperature from 600 to 1000 degreesC for 5 It. The x-ray diffraction profiles showed that the MgGa2O4:Eu3+ powders began to crystallize around 600 degreesC and formed stable MgGa2O4 phase in the temperature range of 600-900 degreesC. The transmission electron microscopy morphology observations revealed that the fired powders exhibit small grain size less than 20 nm. In the PL studies, under ultraviolet (394 nm) excitation, the calcined powders emitted bright red luminescence (615 nm, 5D(0)-->7F(2)), and the powders fired at 900 degreesC were found to have the maximum photoluminescence intensity. The quenching concentration of Eu3+ in MgGa2O4 crystallites was also indicated to be about 5similar to6 mol%.