Detection and Monitoring of Fatigue Cracks in Metallic Structures Using Acoustic Emission: Routes to Quantification of Probability of Detection

被引：2

作者：

Gagar, D. ^{[1
]}

Foote, P. ^{[1
]}

Irving, P. E. ^{[1
]}

机构：

[1] Cranfield Univ, Sch Appl Sci, Cranfield MK43 0AL, Beds, England

来源：

11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2 | 2014年 / 891-892卷

基金：

英国工程与自然科学研究理事会;

关键词：

Acoustic emission; Structural health monitoring; Fatigue crack; Probability of detection;

D O I：

10.4028/www.scientific.net/AMR.891-892.1268

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The performance and reliability of Structural Health Monitoring (SHIM) techniques remain largely unquantified. This is in contrast to the probability of detection (POD) and sensitivity of manual non destructive inspection methods which are well characterised. In this study factors influencing the rates of emission of Acoustic Emission (AE) signals from propagating fatigue cracks were investigated. Fatigue crack growth experiments were performed in 2014 T6 aluminium sheet to observe the effects of changes in crack length, loading spectrum and sample geometry on rates of emission and the probability of detecting and locating the fatigue crack. Significant variation was found in the rates of AE signal generation during crack progression from initiation to final failure. AE signals at any point in the failure process were found to result from different failure mechanisms operating at particular stages in the failure process.

引用

页码：1268 / 1274

页数：7

共 50 条

[1] Detection and Quantification of Fatigue Cracks in Rail Steel Using Acoustic Emission Technique
Li, D.
Kuang, K. S. C.
Koh, C. G.
STRUCTURAL HEALTH MONITORING 2015: SYSTEM RELIABILITY FOR VERIFICATION AND IMPLEMENTATION, VOLS. 1 AND 2, 2015, : 2529 - 2536
[2] Detection of Corrosion Processes and Fatigue Cracks by Means of Acoustic Emission Monitoring
Jagenbrein, Andreas
Tscheliesnig, Peter
Wachsmuth, Janne
Bohse, Juergen
MATERIALS TESTING, 2012, 54 (11-12) : 769 - 778
[3] ACOUSTIC EMISSION MONITORING SYSTEM FOR DETECTION OF CRACKS IN A COMPLEX STRUCTURE
NAKAMURA, Y
MATERIALS EVALUATION, 1971, 29 (01) : 8 - &
[4] Acoustic emission monitoring of short fatigue cracks
You, H
Kwon, OY
Lee, K
NONDESTRUCTIVE CHARACTERIZATION OF MATERIALS IX, 1999, 497 : 48 - 53
[5] Detection of a fatigue crack using acoustic emission
Bousseau, M
LeGuen, F
INTERNATIONAL CONFERENCE ON FATIGUE OF WELDED COMPONENTS AND STRUCTURES, 1996, : 331 - 339
[6] Detection of cracks in concrete by acoustic emission
Sklarczyk, C.
Gries, H.
Waschkies, E.
Proceedings of the International Workshop on Testing During Concrete Construction, 1991,
[7] DETECTION OF ROLLING-CONTACT SUBSURFACE FATIGUE CRACKS USING ACOUSTIC-EMISSION TECHNIQUE
YOSHIOKA, T
LUBRICATION ENGINEERING, 1993, 49 (04): : 303 - 308
[8] Improving of acoustic emission signal detection for fatigue fracture monitoring
Danyuk, A.
Rastegaev, I.
Pomponi, E.
Linderov, M.
Merson, D.
Vinogradov, A.
PROCEEDINGS OF THE 3RD INTERNATIONAL CONFERENCE ON DYNAMICS AND VIBROACOUSTICS OF MACHINES (DVM2016), 2017, 176 : 284 - 290
[9] ACOUSTIC-EMISSION MONITORING OF FATIGUE CRACKS IN COMPONENTS AND STRUCTURES DURING SEVERE FATIGUE NOISE ENVIRONMENT
HORAK, CR
WEYHRETER, AF
MATERIALS EVALUATION, 1977, 35 (03) : S11 - S11
[10] Fatigue crack monitoring of aircraft structures using acoustic emission
Rovik, CL
Vaughn, SG
Hill, EV
Demeski, RJ
SECOND INTERNATIONAL CONFERENCE ON NONLINEAR PROBLEMS IN AVIATION & AEROSPACE VOL 1 AND 2, 1999, : 657 - 664

← 1 2 3 4 5 →