Steam Oxidation Resistance of Slurry Aluminum and Aluminum/Silicon Coatings on Steel for Ultrasupercritical Steam Turbines

被引：19

作者：

Boulesteix, Claire ^{[1
]}

Pedraza, Fernando ^{[1
]}

Proy, Manuel ^{[1
]}

Lasanta, Isabel ^{[2
]}

de Miguel, Teresa ^{[2
]}

Illana, Andrea ^{[2
]}

Javier Perez, Francisco ^{[2
]}

机构：

[1] Univ La Rochelle, LASIE, UMR CNRS 7356, F-17042 La Rochelle 1, France

[2] Univ Complutense Madrid, Fac Ciencias Quim, Grp Ingn Superficies & Mat Nanoestruct, E-28040 Madrid, Spain

来源：

OXIDATION OF METALS | 2017年 / 87卷 / 3-4期

关键词：

Steam; Oxidation; Al and Al/Si coatings; Steel; AUSTENITIC STAINLESS-STEELS; HIGH-TEMPERATURE OXIDATION; CVD-FBR TECHNOLOGY; FERRITIC STEELS; MICROSTRUCTURE EVOLUTION; MECHANICAL-PROPERTIES; SULFIDATION BEHAVIOR; POWER-PLANTS; AL; PRECIPITATION;

D O I：

10.1007/s11085-017-9726-4

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Aluminum and aluminum/silicon coatings were deposited on ferritic-martensitic P92 and austenitic IN-800HT steels in a single-step process from an environmentally friendly slurry. A B2-FeAl phase formed on both the Al and the Al/Si coatings formed on P92. On IN-800HT, both Al and Al/Si grew a B2-(Fe,Ni)Al matrix. An additional zeta 2-(Fe,Ni)(3)Al-10 phase was also detected in the Al/Si coatings. The behavior of these coatings was then studied in steam at 650 A degrees C and 1 bar for 2000 h. The uncoated P92 displayed a significant mass gain compared to the coated ones. The coatings also reduced the mass gains of the uncoated IN-800HT but to a lesser extent than in P92. The reduction in kinetics of the coated specimens was attributed to the major formation of a protective alpha-Al2O3 oxide.

引用

页码：469 / 479

页数：11

共 50 条

[1] Steam Oxidation Resistance of Slurry Aluminum and Aluminum/Silicon Coatings on Steel for Ultrasupercritical Steam Turbines
Claire Boulesteix
Fernando Pedraza
Manuel Proy
Isabel Lasanta
Teresa de Miguel
Andrea Illana
Francisco Javier Pérez
Oxidation of Metals, 2017, 87 : 469 - 479
[2] Steam Oxidation and Chromia Evaporation in Ultrasupercritical Steam Boilers and Turbines
Holcomb, Gordon R.
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2009, 156 (09) : C292 - C297
[3] Investigation of the control dynamics of turbines at the ultrasupercritical parameters of steam
Bulkin, A.E.
Kalashnikov, A.A.
Teploenergetika, 1996, (05): : 43 - 46
[4] Concept of turbines for ultrasupercritical, supercritical, and subcritical steam conditions
Mikhailov V.E.
Khomenok L.A.
Pichugin I.I.
Kovalev I.A.
Bozhko V.V.
Vladimirskii O.A.
Zaitsev I.V.
Kachuriner Y.Y.
Nosovitskii I.A.
Orlik V.G.
Thermal Engineering, 2017, 64 (11) : 787 - 793
[5] HIGH TEMPERATURE STEAM CORROSION OF MICROARC OXIDATION COATINGS ON 6061 ALUMINUM ALLOY AT 300°C/3 MPa STEAM
Qu, Yao
Yang, Chaolin
Jin, Xiaoyue
Du, Jiancheng
Xue, Wenbin
SURFACE REVIEW AND LETTERS, 2021, 28 (01)
[6] Control valves and cascades for the first stages of turbines with ultrasupercritical steam parameters
Zaryankin A.E.
Rogalev N.D.
Rogalev A.N.
Garanin I.V.
Osipov S.K.
Grigoriev E.Y.
Thermal Engineering, 2016, 63 (6) : 422 - 429
[7] Effect of silicon on the steam oxidation resistance of a 9% Cr heat resistant steel
Ishitsuka, T
Inoue, Y
Ogawa, H
OXIDATION OF METALS, 2004, 61 (1-2): : 125 - 142
[8] Effect of Silicon on the Steam Oxidation Resistance of a 9%Cr Heat Resistant Steel
T. Ishitsuka
Y. Inoue
H. Ogawa
Oxidation of Metals, 2004, 61 : 125 - 142
[9] Long exposure steam oxidation testing and mechanical properties of slurry aluminide coatings for steam turbine components
Agüero, A
Muelas, R
Pastor, A
Osgerby, S
SURFACE & COATINGS TECHNOLOGY, 2005, 200 (5-6): : 1219 - 1224
[10] STEAM OXIDATION OF SILICON
TAFT, EA
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1989, 136 (11) : 3476 - 3478

← 1 2 3 4 5 →