Surface hardening of carbon steel using high powered YAG laser

A high powered YAG laser with kaleidoscope for surface modification was applied to the surface hardening of carbon steels containing 0. 18-0.54 wt% C without the absorbents, and the relationships between laser processing and surface hardening were investigated by hardness and microstructure. The structure of the hardened zone underwent complete martensitic transformation in all of the carbon steels tested, and its hardness increased with greater carbon content. Under identical irradiated conditions, the hardened zone expanded with increasing carbon content. A hardened zone extending from the surface to a depth of 1.0 mm was obtained at a laser power of 1.0 kW and a scanning speed of 1 mm/sec. It was found that in the surface hardening of carbon steels, a high powered YAG laser can be used to control the hardened zone by selecting the appropriate irradiation conditions, however, the hardened zone was affected by the assistant gas and the flow rate.