Effect of Ce addition on microstructures and mechanical properties of A380 aluminum alloy prepared by squeeze-casting

The effect of cerium (Ce) addition on the eutectic Si, beta-Al5FeSi phase, and the tensile properties of A380 alloy specimens prepared by squeeze-casting were studied by optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The experimental results showed that Ce more effectively modified the eutectic Si and refined the beta-Al5FeSi. The refinement effect significantly increased under a specific pressure of 100 MPa with the addition of Ce from 0.1wt% to 0.9wt%. In contrast, the average length and the aspect ratio of the eutectic Si and beta-Al5FeSi exhibited their optimal values when the content of the added Ce was greater than 0.5wt%. Needle-like Al8Cu4Ce was precipitated with the addition of excessive Ce; hence, the mechanical properties of A380 gradually decreased with increasing Ce content in the range from 0.3wt% to 0.9wt%.