Corrosion Failure of AISI4340 Steel in Oxygen-Containing Aqueous Chloride Solution

被引：3

作者：

Zhang, Ping ^{[1
]}

Shi, Yafei ^{[2
]}

Zhao, Hanqing ^{[2
]}

Zhang, Fulin ^{[2
]}

Zhang, Guoqiang ^{[1
]}

Rao, Sixian ^{[2
]}

机构：

[1] Hunan Univ, Coll Civil Engn, Changsha 410082, Hunan, Peoples R China

[2] Anhui Univ Technol, Sch Mech Engn, Maanshan 243002, Peoples R China

来源：

INTERNATIONAL JOURNAL OF CORROSION | 2019年 / 2019卷

基金：

国家高技术研究发展计划(863计划);

关键词：

FATIGUE-CRACK-GROWTH; HIGH-STRENGTH STEEL;

D O I：

10.1155/2019/5318290

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Stress corrosion cracking behavior of 4340 steel in oxygen-containing or chloride containing aqueous solution was researched, the tensile experiment results indicated 100 degrees C deaerated distilled water, the rupture of 4340 steel mainly belongs to ductile fracture, the addition of oxygen or chloride would increase the SCC tendency of 4340 steel and transformed the rupture mechanism from ductile fracture to brittle rupture, the existence of oxygen or chloride would decrease K-ISCC of 4340 steel in 100 degrees C aqueous solution slightly, the simultaneous action of oxygen and chloride existed, and the simultaneous action would further increase the SCC tendency of 4340 steel in aqueous solution.

引用

页数：6

共 50 条

[1] Adiabatic shear and dynamic failure criterion for AISI4340 steel
Ma, Li
Zheng, Jin-Yang
Hu, Yang
Li, Xiang
Binggong Xuebao/Acta Armamentarii, 2010, 31 (SUPPL. 1): : 79 - 83
[2] Microstructure-Toughness Relationship in AISI4340 Steel
Saeidi, N.
Ekrami, A.
DIFFUSION IN SOLIDS AND LIQUIDS VI, PTS 1 AND 2, 2011, 312-315 : 110 - 115
[3] Effects of Applied Stresses on Martensite Transformation in AISI4340 Steel
Seok-jae LEE
Young-kook LEE
JournalofIronandSteelResearch(International), 2007, (06) : 63 - 67
[4] Effects of Applied Stresses on Martensite Transformation in AISI4340 Steel
Hong-zhuang Zhao
Seok-jae Lee
Young-kook Lee
Xiang-hua Liu
Guo-dong Wang
Journal of Iron and Steel Research International, 2007, 14 : 63 - 67
[5] Stress-Corrosion Cracking of AISI 4340 Steel in Aqueous Environments
Sergiy Kalnaus
Jixi Zhang
Yanyao Jiang
Metallurgical and Materials Transactions A, 2011, 42 : 434 - 447
[6] Stress-Corrosion Cracking of AISI 4340 Steel in Aqueous Environments
Kalnaus, Sergiy
Zhang, Jixi
Jiang, Yanyao
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (02): : 434 - 447
[7] The Numerical Simulation Technology in the Cutting Process of Alloy Steel AISI4340
Wang, Shigang
Yu, Yueqiang
Gao, Fusheng
Li, Xibing
ADVANCES IN MATERIALS PROCESSING X, 2012, 500 : 180 - 185
[8] Analytical modelling of residual stresses in orthogonal machining of AISI4340 steel
Agrawal, Saurabh
Joshi, Suhas S.
JOURNAL OF MANUFACTURING PROCESSES, 2013, 15 (01) : 167 - 179
[9] Determining the Effect of Material Hardness During the Hard Turning of AISI4340 Steel
Kambagowni V.
Chitla R.
Challa S.
Journal of The Institution of Engineers (India): Series D, 2018, 99 (2) : 185 - 192
[10] Corrosion behaviour of iron and AISI 304 stainless steel in tungstate aqueous solutions containing chloride
Azambuja, DS
Martini, EMA
Müller, IL
JOURNAL OF THE BRAZILIAN CHEMICAL SOCIETY, 2003, 14 (04) : 570 - 576

← 1 2 3 4 5 →