Investigation of stress field and failure mode of plasma sprayed Al2O3-13%TiO2 coatings under thermal shock

被引：21
|
作者：
Wang, Y. [1 ]
Tian, W. [1 ]
Yang, Y. [1 ]
Li, C. G. [1 ]
Wang, L. [1 ]
机构：
[1] Harbin Inst Technol, Dept Mat Sci, Nano Surface Engn Lab, Harbin 150001, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2009年 / 516卷 / 1-2期
关键词：
Plasma spray; Al2O3-13%TiO2 coating; Thermal shock; Finite element method; FINITE-ELEMENT-ANALYSIS; RESIDUAL-STRESSES; BARRIER COATINGS; COMPOSITE COATINGS; BEHAVIOR; FRACTURE; ALUMINA;
D O I：
10.1016/j.msea.2009.03.041
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The stress field and failure mode of plasma sprayed Al2O3-13%TiO2 coatings under thermal shock were analyzed by experimental and numerical investigations in this paper. Two kinds of nanostructured coatings were derived from reconstituted nanostructured feedstocks and one kind of conventional coating was deposited with commercial fused and crushed feedstock. Testing results showed that the nanostructured coatings exhibited improved thermal shock resistance than the conventional coating. The failure modes of coatings predicted by numerical analysis had a good consistency with the experimental results. The effects of interface morphology and coating defects on thermal stresses were also discussed in this paper. The improved thermal shock resistance of nanostructured coatings was related to their pre-existing spherical pores, reduced cracks and microstructures. (C) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码：103 / 110
页数：8
相关论文
共 50 条
  • [1] Microstructure, spallation and corrosion of plasma sprayed Al2O3-13%TiO2 coatings
    Wang, You
    Tian, Wei
    Zhang, Tao
    Yang, Yong
    CORROSION SCIENCE, 2009, 51 (12) : 2924 - 2931
  • [2] Indentation properties of plasma sprayed Al2O3-13% TiO2 nanocoatings
    Rodriguez, J.
    Rico, A.
    Otero, E.
    Rainforth, W. M.
    ACTA MATERIALIA, 2009, 57 (11) : 3148 - 3156
  • [3] Thermal shock properties and failure mechanism of plasma sprayed Al2O3/TiO2 nanocomposite coatings
    Zhai, CS
    Wang, J
    Li, F
    Tao, JC
    Yang, Y
    Sun, BD
    CERAMICS INTERNATIONAL, 2005, 31 (06) : 817 - 824
  • [4] Sliding wear and electrochemical corrosion behavior of plasma sprayed nanocomposite Al2O3-13%TiO2 coatings
    Tian, Wei
    Wang, You
    Zhang, Tao
    Yang, Yong
    MATERIALS CHEMISTRY AND PHYSICS, 2009, 118 (01) : 37 - 45
  • [5] Corrosion of plasma sprayed NiCrAl/Al2O3-13 wt-%TiO2 coatings with and without sealing
    Zhang, J. J.
    Wang, Z. H.
    Lin, P. H.
    Si, L. Q.
    Shen, G. J.
    Zhou, Z. H.
    Jiang, S. Q.
    Lu, W. H.
    SURFACE ENGINEERING, 2012, 28 (05) : 345 - 350
  • [6] Toughening and strengthening mechanism of plasma sprayed nanostructured Al2O3-13 wt.%TiO2 coatings
    Tian, Wei
    Wang, You
    Yang, Yong
    Li, Chonggui
    SURFACE & COATINGS TECHNOLOGY, 2009, 204 (05): : 642 - 649
  • [7] Phase evolution of plasma sprayed Al2O3-13%TiO2 coatings derived from nanocrystalline powders
    Lu, Xue-cheng
    Yan, Dian-ran
    Yang, Yong
    Dong, Yan-chun
    He, Ji-ning
    Zhang, Jian-xin
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (10) : 2951 - 2956
  • [8] Microstructure and properties of Al2O3-13%TiO2 coatings sprayed using nanostructured powders
    ZHANG Jianxin
    Rare Metals, 2007, (04) : 391 - 397
  • [9] Nlicrostructure and properties of Al2O3-13%TiO2 coatings sprayed using nanostructured powders
    Zhang Jianxin
    He Jining
    Dong Yanchun
    Li Xiangzhi
    Yan Dianran
    RARE METALS, 2007, 26 (04) : 391 - 397
  • [10] Thermal-shock resistance of plasma sprayed Al2O3-13 wt%TiO2 coating evaluated by residual strength method
    Wang, Miqi
    Zhou, Zehua
    Yi, Yu
    Wang, Zehua
    SURFACE & COATINGS TECHNOLOGY, 2019, 375 : 888 - 893
12345