A multi-scale damage model for fatigue accumulation due to short cracks nucleation and growth

被引：31
|
作者：
Sun, Bin [1 ]
Li, Zhaoxia [1 ]
机构：
[1] Southeast Univ, Dept Engn Mech, Jiangsu Key Lab Engn Mech, Nanjing 210096, Jiangsu, Peoples R China
来源：
ENGINEERING FRACTURE MECHANICS | 2014年 / 127卷
基金：
中国国家自然科学基金;
关键词：
Short crack; Fatigue damage; Multi-scale damage model; Fatigue life; NUMERICAL DENSITY; BEHAVIOR; INITIATION; EVOLUTION; PROPAGATION; MECHANICS; MICROSTRUCTURE; MICRODAMAGE; SIMULATION; CONTINUUM;
D O I：
10.1016/j.engfracmech.2014.06.014
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
A multi-scale fatigue damage evolution model is proposed for describing both the behaviour of short fatigue cracks nucleation and growth in micro-scale and fatigue damage evolution reflecting the progressive deterioration process of metal components and structures in macro-scale. The model is verified through the experimental data of fatigue damage. It was found that, the model can offer a new reasonable explanation of the effect of load sequence on fatigue life, and also can predict the fatigue life during fatigue damage accumulation due to short cracks nucleation and growth in metal components and structures. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：280 / 295
页数：16
相关论文
共 50 条
  • [1] Multi-scale fatigue damage model for micro-cracks nucleation and growth and its application
    Sun, Bin
    Li, Zhaoxia
    Dongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Southeast University (Natural Science Edition), 2014, 44 (02): : 333 - 338
  • [2] Multi-scale model for linking collective behavior of short and long cracks to continuous average fatigue damage
    Sun, Bin
    Xu, You-Lin
    Li, Zhaoxia
    ENGINEERING FRACTURE MECHANICS, 2016, 157 : 141 - 153
  • [3] A Multi-scale Corrosion Fatigue Damage Model of Aluminum Alloy Considering Multiple Pits and Cracks
    Sun, Bin
    Zheng, Yang
    Li, Zhaoxia
    ACTA MECHANICA SOLIDA SINICA, 2018, 31 (06) : 731 - 743
  • [4] A Multi-scale Corrosion Fatigue Damage Model of Aluminum Alloy Considering Multiple Pits and Cracks
    Bin Sun
    Yang Zheng
    Zhaoxia Li
    Acta Mechanica Solida Sinica, 2018, 31 : 731 - 743
  • [5] Multi-scale fatigue model and image-based simulation of collective short cracks evolution process
    Sun, Bin
    Xu, You-Lin
    Li, Zhaoxia
    COMPUTATIONAL MATERIALS SCIENCE, 2016, 117 : 24 - 32
  • [6] THE NUCLEATION AND GROWTH OF SHORT FATIGUE CRACKS BOTH AT PLAIN SURFACES AND NOTCHES
    GUIU, F
    STEVENS, RN
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1990, 13 (06) : 625 - 635
  • [7] A multi-scale model from microscopic cracks to macroscopic damage of concrete at elevated temperatures
    Sun, Bin
    Guo, Tong
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2024, 33 (03) : 177 - 192
  • [8] Variability on nucleation and growth of short fatigue cracks due to material anisotropy in aluminum 2024-T351
    Makas, Admir
    Avallone, Jaclyn
    MacKinnon, Ross
    Atodaria, Ikshwaku
    Peralta, Pedro
    JOURNAL OF INTELLIGENT MATERIAL SYSTEMS AND STRUCTURES, 2013, 24 (17) : 2148 - 2167
  • [9] Multi-scale damage model for mechanical High Cycle Fatigue (HCF) of short glass fibre reinforced thermoplastics (SGFRTP)
    Krairi, Anouar
    Doghri, Issam
    FATIGUE DESIGN 2013, INTERNATIONAL CONFERENCE PROCEEDINGS, 2013, 66 : 759 - 765
  • [10] Multi-scale fatigue damage model for steel structures working under high temperature
    Guo, Huajing
    Sun, Bin
    Li, Zhaoxia
    ACTA MECHANICA SINICA, 2019, 35 (03) : 615 - 623
12345