Preparation and mechanical properties of highly densified nanocrystalline Al

被引：75
|
作者：
Sun, XK [1 ]
Cong, HT
Sun, M
Yang, MC
机构：
[1] Chinese Acad Sci, Inst Met Sci, State Key Lab RSA, Shenyang 110015, Peoples R China
[2] PR China Med Univ, Dept Phys, Shenyang 110001, Peoples R China
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 3A期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1007/s11661-000-0043-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The preparation of highly densified nanocrystalline (NC) Al was conducted in three steps. First, the NC Al powder was synthesized by an active H-2 plasma evaporation method. Then, the NC Al powder was compacted at room temperature into disk-shaped samples with a 25-mm diameter and 2-mm thickness and was sintered at 620 degrees C or 635 degrees C (sintered NC Al), The sintering does not result in grain growth. Finally the sintered NC Al was rolled at room temperature into sheet samples with a 1-mm thickness and 99 pet relative density (cold-deformed NC Al). The microhardnesses and tensile properties of the sintered NC Al and cold-deformed NC Al were tested at room temperature. The results show that their strengths are basically the same, and the yield strengths (sigma(0.2)) and tensile strengths (sigma(b)) are 12 to 16 and 5 to 6 times those of annealed coarse-grained Al, respectively, but the elongation to failure of the cold-deformed NC Al is up to 8 pct, which is 2 times that of the sintered NC Al and higher than that of cold-deformed, coarse-grained Al by 30 pct. The failure features of the sintered NC Al and cold-deformed NC Al belong to typical plastic fracture with ductile dimples, and the mechanism of failure is transgranular shear fracture.
引用
收藏
页码：1017 / 1024
页数：8
相关论文
共 50 条
  • [1] Preparation and mechanical properties of highly densified nanocrystalline Al
    X. K. Sun
    H. T. Cong
    M. C. Yang
    M. Sun
    Metallurgical and Materials Transactions A, 2000, 31 : 1017 - 1024
  • [2] Preparation and mechanical properties of highly densified nanocrystalline Al
    Sun X.K.
    Cong H.T.
    Sun M.
    Yang M.C.
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 2000, 31 (13): : 1017 - 1024
  • [3] Preparation and properties characterization of nanocrystalline Al
    Key Lab. of Advanced Functional Materials, College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
    Cailiao Gongcheng, 2008, 10 (251-253+256):
  • [4] PREPARATION AND PROPERTIES OF HIGHLY DENSIFIED YTTRIUM-BARIUM-COPPER OXIDE
    HOJAJI, H
    BARKATT, A
    HEIN, RA
    MATERIALS RESEARCH BULLETIN, 1988, 23 (06) : 869 - 879
  • [5] Preparation and mechanical properties of nanocrystalline Mn metal
    Shi Jian
    Li Jiangong
    Sun Xiaojun
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (05) : 937 - 940
  • [6] Preparation and mechanical properties of nanocrystalline Mn metal
    Institute of Materials Science and Engineering, Lanzhou University, Lanzhou 730000, China
    Xiyou Jinshu Cailiao Yu Gongcheng, 2007, 5 (937-940): : 937 - 940
  • [7] Preparation and Mechanical Properties of Bulk Nanocrystalline Nickel
    Ba Zhixin
    Lu Chengjie
    Zhang Zhenzhong
    Zhou Jianqiu
    Zhang Shaoming
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (04) : 628 - 632
  • [8] Effect of Pb on the mechanical properties of nanocrystalline Al
    Rajulapati, Koteswararao V.
    Scattergood, Ronald O.
    Murty, Korukonda L.
    Duscher, Gerd
    Koch, Carl C.
    SCRIPTA MATERIALIA, 2006, 55 (02) : 155 - 158
  • [9] Mechanical properties of densified spruce
    Haller, P
    Wehsener, J
    HOLZ ALS ROH-UND WERKSTOFF, 2004, 62 (06) : 452 - 454
  • [10] Processing and mechanical properties of nanocrystalline 5083 Al alloy
    Tellkamp, VL
    Lavernia, EJ
    NANOSTRUCTURED MATERIALS, 1999, 12 (1-4): : 249 - 252
12345