Characterisation and corrosion performance of HVOF sprayed Ni-10 wt-%Ti coatings

被引：5
|
作者：
Verdian, M. M. [1 ]
机构：
[1] Islamic Azad Univ, Najafabad Branch, Dept Mat Engn, Najafabad, Isfahan, Iran
来源：
SURFACE ENGINEERING | 2014年 / 30卷 / 09期
关键词：
Corrosion; HVOF; Ni alloy; Hardness; BEHAVIOR; ALLOYS;
D O I：
10.1179/1743294414Y.0000000310
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Mechanically alloyed Ni-10 wt-% Ti powders were deposited on 1045 steel substrate using high velocity oxy-fuel (HVOF) thermal spraying process. The microstructure and phase composition of coatings were evaluated by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The results showed that the phase composition of feedstock powders was preserved during spraying and only supersaturated Ni(Ti) solid solution was present in the coatings. The hardness measurements showed that the hardness of coatings was about 510 HV (50 g). Tafel polarisation tests performed after 1 h immersion revealed that the corrosion behaviour of HVOF Ni-Ti coatings was not affected by substrate. However, delamination of air plasma sprayed (APS) Ni-10 wt-% Ti coatings and significant corrosion of substrate was observed in similar conditions. For HVOF Ni-Ti coating and after 24 h of immersion time, the corrosion of underlying substrate was observed after polarisation measurements but no delamination of coating occurred.
引用
收藏
页码：670 / 674
页数：5
相关论文
共 50 条
  • [1] Characterisation of HVOF sprayed NiCrAlY-0.4 wt-%CeO2 coatings on superalloys
    Mahesh, R. A.
    Jayaganthan, R.
    Prakash, S.
    SURFACE ENGINEERING, 2008, 24 (05) : 366 - 373
  • [2] Microstructure and wear performance of Ni-10 wt.%Al coatings plasma sprayed on Ni-based superalloys with a sound field
    Wang, Chao
    Gao, Pengfei
    Liu, Tie
    Li, Liangfeng
    Wang, Enze
    Wang, Qiang
    SURFACE & COATINGS TECHNOLOGY, 2019, 370 : 157 - 162
  • [3] Thermal spray coatings of Ni-10 wt-%Al composite powder synthesised by low energy mechanical milling
    Movahedi, B.
    Enayati, M. H.
    Salehi, M.
    SURFACE ENGINEERING, 2009, 25 (04) : 276 - 283
  • [4] Frequency dependence of sound field effect on microstructure and wear performance of plasma sprayed Ni-10 wt.%Al coatings
    Gao, Pengfei
    Liu, Tie
    Wang, Chao
    Wu, Anping
    Li, Zhanliang
    Li, Guojian
    Wang, Qiang
    SURFACE & COATINGS TECHNOLOGY, 2020, 396
  • [5] Hot corrosion behaviour of HVOF sprayed NiCrAlY-0.4 wt-%CeO2 coatings on superalloys in aggressive environment at 900°C
    Mahesh, R. A.
    Rao, G.
    Jayaganthan, R.
    Prakash, S.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2010, 45 (02) : 142 - 149
  • [6] Hot corrosion behaviour of HVOF sprayed Ni3Ti and Ni3Ti
    Reddy, Nagaraja C.
    Koppad, Praveennath G.
    Reddappa, H. N.
    Ramesh, M. R.
    Rahn, E. R.
    Varol, T.
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2019, 7 (02)
  • [7] Coarsening process of coherent β′ precipitates in Fe-10 wt-%Ni-15 wt-% Al and Fe-10 wt-%Ni-15 wt-%Al-1 wt-%Cu alloys
    Rosales-Dorantes, H. J.
    Cayetano-Castro, N.
    Lopez-Hirata, V. M.
    Saucedo-Munoz, M. L.
    Villegas-Cardenas, D.
    Hernandez-Santiago, F.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (12) : 1492 - 1498
  • [8] Corrosion behaviour of HVOF sprayed coatings in seawater
    Kawakita, J
    Fukushima, T
    Kuroda, S
    Kodama, T
    THERMAL SPRAY 2001: NEW SURFACES FOR A NEW MILLENNIUM, 2001, : 1137 - 1142
  • [9] High temperature corrosion behaviour of HVOF sprayed WC-CrC-Ni coatings
    Somasundaram, B.
    Kadoli, Ravikiran
    Ramesh, M. R.
    Ramesh, C. S.
    INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING, 2016, 10 (04) : 400 - 413
  • [10] Investigations on role of HVOF sprayed Co and Ni based coatings to combat hot corrosion
    Sidhu, T. S.
    Prakash, S.
    Agrawal, R. D.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2008, 43 (04) : 335 - 342
12345