Fabrication of Bi2223 bulks with high critical current properties sintered in Ag tubes

Randomly grain oriented Bi2223 sintered bulks are one of the representative superconducting materials having weak-link problem due to very short coherence length particularly along the c-axis, resulting in poor intergrain Jc properties. In our previous studies, sintering and/or post-annealing under moderately reducing atmospheres were found to be effective for improving grain coupling in Bi2223 Sintered bulks. Further optimizations of the synthesis process for Bi2223 sintered bulks were attempted in the present study to enhance their intergrain A. Effects of applied pressure of uniaxial pressing and sintering conditions on microstructure and superconducting properties have been systematically investigated. The best sample showed intergrain Jc of 2.0 kA cm(-2) at 77 K and 8.2 kA cm(-2) at 20K, while its relative density was low similar to 65%. These values are quite high as for a randomly oriented sintered bulk of cuprate superconductors. (C) 2017 Elsevier B.V. All rights reserved.