On the transverse cracking and stiffness degradation of aged angle-ply laminates

被引：18
|
作者：
Tounsi, A.
Amara, K. H.
Benzair, A.
Megueni, A.
机构：
[1] Univ Sidi Bel Abbes, Lab Mat & Hydrol, Sidi Bel Abbes 22000, Algeria
[2] Univ Sidi Bel Abbes, Dept Phys, Sidi Bel Abbes 22000, Algeria
来源：
MATERIALS LETTERS | 2006年 / 60卷 / 21-22期
关键词：
hygrothermal effect; transverse cracking; angle-ply laminates; stress perturbation function; stiffness reduction;
D O I：
10.1016/j.matlet.2006.01.037
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A modified shear lag analysis, taking into account the concept of stress perturbation function, is employed to evaluate the effect of transverse cracks on the stiffness reduction in aged angle-ply laminated composites. The results of this paper represent well the dependence of the degradation of elastic properties on the cracks density, hygrothermal conditions and the fibre orientation of the outer layers. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：2561 / 2564
页数：4
相关论文
共 50 条
  • [1] Stiffness degradation resulting from 90° ply cracking in angle-ply composite laminates
    Pradhan, B
    Kumar, NV
    Rao, NS
    COMPOSITES SCIENCE AND TECHNOLOGY, 1999, 59 (10) : 1543 - 1552
  • [2] MULTIPLE CRACKING IN ANGLE-PLY COMPOSITE LAMINATES
    WANG, J
    KARIHALOO, BL
    JOURNAL OF COMPOSITE MATERIALS, 1995, 29 (10) : 1321 - 1336
  • [3] Finite element analysis of transverse cracking behaviour in hybrid angle-ply composite laminates
    Pradhan, B
    Kumar, NV
    Rao, NS
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1999, 18 (15) : 1428 - 1448
  • [4] Effect of Off – Axis Matrix Cracking on Stiffness of Symmetric Angle-Ply Composite Laminates
    D. G. Katerelos
    L. N. McCartney
    C. Galiotis
    International Journal of Fracture, 2006, 139 : 529 - 536
  • [5] Effect of off - axis matrix cracking on stiffness of symmetric angle-ply composite laminates
    Katerelos, D. G.
    McCartney, L. N.
    Galiotis, C.
    INTERNATIONAL JOURNAL OF FRACTURE, 2006, 139 (3-4) : 529 - 536
  • [6] Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting
    Kashtalyan, M
    Soutis, C
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2000, 31 (04) : 335 - 351
  • [7] Effect of transverse cracking on stiffness reduction of hygrothermal aged cross-ply laminates
    Bouazza, M.
    Tounsi, A.
    Benzair, A.
    Adda-bedia, E. A.
    MATERIALS & DESIGN, 2007, 28 (04) : 1116 - 1123
  • [8] Study of the transverse cracking and stiffness loss in hygrothermal aged cross-ply laminates
    Adda-Bedia, EA
    Tounsi, A
    Amara, KH
    Meftah, S
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2004, 20 : 111 - 113
  • [9] Effect of transverse cracks on the effective thermal expansion coefficient of aged angle-ply composites laminates
    Fellah, M.
    Tounsi, A.
    Amara, K. H.
    Bedia, E. A. Adda
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2007, 48 (01) : 32 - 40
  • [10] Effect of transverse cracks on the mechanical properties of angle-ply composites laminates
    Amara, K
    Tounsi, A
    Megueni, A
    Adda-Bedia, EA
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2006, 45 (01) : 72 - 78
12345