Scattering of phonons by a spatially correlated system of Fe atoms and the low-temperature anomaly of thermal conductivity in HgSe:Fe crystals

The thermal conductivity kappa of HgSe:Fe samples with various content N-Fe of Fe impurity was studied in the temperature range of 8-60 K. It was found that the dependence of the thermal conductivity kappa on N-Fe is unconventional at low temperatures. For T < 12 K, the value of kappa first decreases with an increase in the Fe concentration up to N-Fe = 5 x 10(18) cm(-3) and then increases and attains a maximum for N-Fe = (1-2) x 10(19) cm(-3). A further increase in Fe concentration brings about a steady decrease in thermal conductivity. The electron- and phonon-related thermal conductivity of HgSe:Fe crystals with consideration of the effects caused by the ordering of trivalent Fe ions was analyzed. It is shown that both the electron- and phonon-related contributions to thermal conductivity at low temperatures are increasing functions of Fe concentration in the range of 5 x 10(18) < N-Fe < (1-2) x 10(19) cm(-3). However, the electronic contribution is too small to account for the experimental increase in thermal conductivity. An analysis of the lattice contribution to thermal conductivity showed that an anomalous increase in thermal conductivity is caused by a reduction in the Rayleigh scattering of phonons by a system of Fe ions with mixed valence and is related to the spatial ordering of Fe3+ ions. (C) 2000 MAIK "Nauka/Interperiodica".