Fatigue analysis of multiple site damage in lap joint specimens

被引：1
|
作者：
Wang, HL [1 ]
Grandt, AF [1 ]
机构：
[1] Purdue Univ, Sch Aeronaut & Astronaut, W Lafayette, IN 47907 USA
来源：
FATIGUE AND FRACTURE MECHANICS: 30TH VOLUME | 2000年 / 1360卷
关键词：
lap joints; load transfer mechanism; hole expansion; rivets; multiple site damage; fatigue crack propagation; life prediction;
D O I：
10.1520/STP13405S
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This paper describes research to determine the influence of multiple-site damage on the fatigue life of lap joint specimens. Multiple-site damage is an important concern in aging aircraft and deals with determining failure conditions for multiple crack configurations. The goal of this paper is to determine the fatigue life fur a mechanically fastened joint with multiple fatigue cracks located along one row of rivet holes. A predictive model for the fatigue life is evaluated with the results of several precracked specimens tested to failure under constant amplitude loading. predictions for the growth and coalescence of individual cracks in specimens with various initial crack configurations and applied stress levels agree well with the experimental results.
引用
收藏
页码：214 / 226
页数：13
相关论文
共 50 条
  • [1] Study on multiple site damage fatigue crack growth of corroded lap joint
    Chen, Yueliang
    Yu, Dazhao
    Duan, Chengmei
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2007, 21 (SUPPL.): : 95 - 99
  • [2] A Numerical Analysis of Riveted Lap Joint Containing Multiple-site Damage
    Yu, Dazhao
    APPLIED MATHEMATICS & INFORMATION SCIENCES, 2013, 7 (02): : 699 - 704
  • [3] Finite element analysis of stress intensity factors of lap joint with multiple site damage
    Chen, Yue-Liang
    Yu, Da-Zhao
    Yang, Mao-Sheng
    Hu, Jia-Lin
    Hangkong Xuebao/Acta Aeronautica et Astronautica Sinica, 2007, 28 (03): : 615 - 619
  • [4] The characteristics of multi-site fatigue damage in the fuselage riveted lap splice joint
    Piascik, RS
    Willard, SA
    ICAF 97: FATIGUE IN NEW AND AGEING AIRCRAFT, VOLS I AND II: VOL I: LECTURE PAPERS, VOL II: POSTER PAPERS, 1997, : 93 - 114
  • [5] Corrosion fatigue and multiple site damage reliability analysis
    Shi, P
    Mahadevan, S
    INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (06) : 457 - 469
  • [6] Early stages of fatigue damage in riveted Alclad 2024-T3 aluminum alloy lap joint specimens
    Fine, ME
    Connor, ZM
    Achenbach, JD
    NONDESTRUCTIVE EVALUATION (NDE) AND MATERIAL PROPERTIES IV, 1999, : 1 - 9
  • [7] Experiments and model predictions for fatigue crack propagation in riveted lap-joints with multiple site damage
    Galatolo, R.
    Lazzeri, R.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (03) : 307 - 319
  • [8] NUMERICAL MODAL SENSITIVITY ANALYSIS FOR FATIGUE DAMAGE ACCUMULATION IN ADHESIVELY BONDED LAP-JOINT
    Palanisamy, Rajendra Prasath
    Banerjee, Portia
    Haq, Mahmood
    Deng, Yiming
    PROCEEDINGS OF ASME 2021 INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION (IMECE2021), VOL 1, 2021,
  • [9] Probabilistic fatigue damage prognosis of lap joint using Bayesian updating
    Peng, Tishun
    He, Jingjing
    Xiang, Yibing
    Liu, Yongming
    Saxena, Abhinav
    Celaya, Jose
    Goebel, Kai
    JOURNAL OF INTELLIGENT MATERIAL SYSTEMS AND STRUCTURES, 2015, 26 (08) : 965 - 979
  • [10] Linkup strength of 2024-T3 bolted lap joint panels with multiple-site damage
    Hijazi, AL
    Smith, BL
    Lacy, TE
    JOURNAL OF AIRCRAFT, 2004, 41 (02): : 359 - 364
12345