The Micro-hardness of Heat Treated Carbon Steel

被引：10

作者：

Petrik, Jozef ^{[1
]}

机构：

[1] Tech Univ Kosice, Met Fac, Dept Integrated Management, Kosice 04200, Slovakia

来源：

MATERIALS SCIENCE-MEDZIAGOTYRA | 2014年 / 20卷 / 01期

关键词：

carbon steel; heat treatment; mechanical properties; LOAD;

D O I：

10.5755/j01.ms.20.1.4017

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The aim of the submitted work is to study the influence of applied loads ranging from 0.09807 N to 0.9807 N on measured values of micro-hardness of heat treated carbon steel. The influence of applied load on measured value of micro-hardness was evaluated by Meyer's index n, PSR method and by Analysis of Variance (ANOVA). The influence of the load on the measured value of micro-hardness is statistically significant and the relationship between applied load and micro-hardness manifests the moderate reverse ISE. As far as the relationship between measured hardness and load independent "true hardness", the best fit was obtained between HV0.05 and "true hardness" calculated using index a(2).

引用

页码：21 / 24

页数：4

共 50 条

[1] Micro-hardness of the teeth
Singh, VR
Bhalla, ST
IEEE-EMBS ASIA PACIFIC CONFERENCE ON BIOMEDICAL ENGINEERING - PROCEEDINGS, PTS 1 & 2, 2000, : 542 - 543
[2] A MICRO-HARDNESS TESTER
LLOYD, H
JEFFREY, R
JOURNAL OF SCIENTIFIC INSTRUMENTS, 1947, 24 (07): : 186 - 189
[3] Micro-hardness and adhesion of boron carbon nitride coatings
Hou, QR
Gao, J
MODERN PHYSICS LETTERS B, 1997, 11 (16-17): : 749 - 756
[4] Influence of Different Material of Penetrator on Micro-hardness of Steel Target
Tian, Kaiwen
Zhu, Lijun
Wang, Zhenming
Shi, Wenlu
Zou, Minming
Shi, Honggang
FRONTIERS OF MANUFACTURING SCIENCE AND MEASURING TECHNOLOGY III, PTS 1-3, 2013, 401 : 639 - 642
[5] MICRO-HARDNESS TESTING OF METALS
DUNN, FJ
WHITAKER, P
DESTRYCKER, RE
JOURNAL OF THE INSTITUTE OF METALS, 1948, 74 (12): : 736 - &
[6] Micro-hardness and adhesion of diamond-like carbon films
Hou, QR
Gao, J
MODERN PHYSICS LETTERS B, 1997, 11 (16-17): : 757 - 764
[7] Micro-Hardness and Adhesion of Diamond-Like Carbon Films
Mod Phys Lett B, 16-17 (757):
[8] MICRO-HARDNESS TESTING OF METALS
TAYLOR, EW
JOURNAL OF THE INSTITUTE OF METALS, 1948, 74 (10): : 493 - &
[9] Dependence of micro-hardness on deformation of deep-drawing steel sheets
Cotterell, M
Schambergerova, J
Ziegelheim, J
Janovec, J
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2002, 124 (03) : 293 - 296
[10] Two-dimensional mapping of micro-hardness increase on surface treated steel determined by photothermal deflection microscopy
Crossa Archiopoli, Ulises
Mingolo, Nelida
Martinez, Oscar E.
SURFACE & COATINGS TECHNOLOGY, 2011, 205 (8-9): : 3087 - 3092

← 1 2 3 4 5 →