Evaluation of dynamic modulus measurement for C/C-SiC composites at different temperatures

The determination of elastic properties at application temperature is fundamental for the design of fibre reinforced ceramic composite components. An attractive method to characterize the flexural modulus at room and high temperature under specific atmosphere is the nondestructive Resonant Frequency Damping Analysis (RFDA). The objective of this paper was to evaluate and validate the modulus measurement via RFDA for orthotropic C/C-SiC composites at the application temperature. At room temperature flexural moduli of C/C-SiC with 0/90 degrees reinforcement were measured under quasi-static 4-point bending loads and compared with dynamic moduli measured via RFDA longitudinally to fibre direction. The dynamic modulus of C/C-SiC was then measured via RFDA up to 1250 degrees C under flowing inert gas and showed an increase with temperature which fitted with literature values. The measured fundamental frequencies were finally compared to those resulting from numerical modal analyses. Dynamic and quasi-static flexural moduli are comparable and the numerical analyses proved that bending modes are correctly modeled by means of dynamic modulus measured via RFDA. The nondestructive RFDA as well as the numerical modeling approach are suitable for evaluation of C/C-SiC and may be transferred to other fibre reinforced ceramic composite materials.