Study on the process of Carbon Nanotubes modified Urea-Formaldehyde Resin Adhesive

被引：0
|
作者：
Zhang, Shaobo [1 ]
Wang, Yu [1 ]
Huang, Jintian [1 ]
机构：
[1] Inner Mongolia Agr Univ, Coll Mat Sci & Art Design, Hohhot 010018, Inner Mongolia, Peoples R China
来源：
PROCEEDINGS OF THE 3RD INTERNATIONAL CONFERENCE ON MATERIAL, MECHANICAL AND MANUFACTURING ENGINEERING | 2015年 / 27卷
关键词：
Urea-formaldehyde; Carbon Nanotubes; Optimal solution;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Using mechanical blending of carbon nanotubes (CNTs) composite urea-formaldehyde (UF) resin adhesives. The ultrasonic time, the amount of CNTs, ultrasonic power orthogonal experi ment was carried out. It is concluded that the important order of effect factors on free formaldehyde emission to UF resin adhesives: the amount of carbon nanotubes, ultrasonic time, ultrasonic frequen cy; The important order of effect factors on the shear strength of UF resin adhesives is ultrasonic po wer, the amount of CNTs, ultrasonic time; Preparation of composite CNTs/UF resin adhesives the o ptimal solution is: ultrasonic time of 30 min, ultrasonic power of 600 W, the amount of CNTs of 0.3 g.
引用
收藏
页码：1408 / 1411
页数：4
相关论文
共 50 条
  • [1] Study on the Influence of Modified Multi-Walled Carbon Nanotubes to the Shear Strength of Urea-Formaldehyde Resin Adhesive
    Huang, Jintian
    Tie, Kunling
    Pan, Yanfei
    [J]. ASIAN JOURNAL OF CHEMISTRY, 2013, 25 (14) : 7997 - 8000
  • [2] Preparation and formaldehyde emission and bonding performance of novel modified urea-formaldehyde resin adhesive
    Gao, Zhenzhong
    Yue, Chao
    Cao, Haibo
    Wang, Xiaobo
    Zhu, Xiaofeng
    Lin, Ruihang
    [J]. MECHATRONICS AND INTELLIGENT MATERIALS II, PTS 1-6, 2012, 490-495 : 3476 - +
  • [3] Particulate reinforcement and formaldehyde adsorption of modified nanocrystalline cellulose in urea-formaldehyde resin adhesive
    Zhang, Hao
    She, Ying
    Song, Shuping
    Lang, Qian
    Pu, Junwen
    [J]. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2013, 27 (09) : 1023 - 1031
  • [4] Thermal Analysis Study of Modified Urea-Formaldehyde Resin
    Hong, Wei
    Meng, Mianwu
    Gao, Dingding
    Liu, Qingye
    Kang, Caiyan
    Huang, Siyu
    Zhou, Zhenming
    Chen, Chunqiang
    [J]. POLYMER-KOREA, 2016, 40 (05) : 707 - 713
  • [5] Particulate reinforcement and formaldehyde adsorption of modified nanocrystalline cellulose in urea-formaldehyde resin adhesive
    [J]. Pu, J. (pujunwen@126.com), 1600, Taylor and Francis Ltd. (27):
  • [6] Investigation of the stability of the modified urea-formaldehyde resin
    Kurta, SA
    Fedorchenko, SV
    Chaber, MV
    [J]. POLIMERY, 2004, 49 (01) : 49 - 51
  • [7] DURABILITY OF UREA-FORMALDEHYDE RESIN ADHESIVE - EFFECT OF PH OF THE ADHESIVE-RESIN LAYER
    YAMAGUCHI, H
    HIGUCHI, M
    SAKATA, I
    [J]. MOKUZAI GAKKAISHI, 1989, 35 (09): : 801 - 806
  • [8] Evaluation of melamine-modified urea-formaldehyde resin for plywood flooring adhesive application
    Oh, Yong-Sung
    Kim, Kyung-Hee Kim
    [J]. Scientia Forestalis/Forest Sciences, 2011, (90): : 199 - 203
  • [9] Evaluation of Melamine-Modified Urea-Formaldehyde Resin for Plywood Flooring Adhesive Application
    Oh, Yong-Sung
    Kim, Kyung-Hee
    [J]. SCIENTIA FORESTALIS, 2011, 39 (90): : 199 - 203
  • [10] Properties of Particleboard Manufactured with Modified Urea-formaldehyde Resin
    Zhang, Jizhi
    Li, Jianzhang
    Zhang, Shifeng
    [J]. ADVANCES IN COMPOSITES, PTS 1 AND 2, 2011, 150-151 : 1135 - 1138
12345