Evaluation of Activated Carbon Fiber Applied in Supercapacitor Electrodes

This study uses rayon woven fabrics as the raw material for activated carbon fabrics (ACFs), which were manufactured by oxidation, carbonization and activation engineering in a continuous semi-open high-temperature furnace. First, the activated carbon fabrics are prepared under two specific manufacturing conditions with different production rates and flow rates of steam activation at 1000 degrees C. Then the electrochemical prosperities of the ACFs are evaluated by a three-electrode device. The experimental results show that the BET specific surface area and electrical capacitance are higher with a lower production rate. Moreover, the steam activator higher flow rate under the proposed approach. ACFs with a 2332.1 m(2)/g specific surface area and 78.7 % mesopore ratio result in a higher electronic conductivity of 430.4 F/g at the low rate charge (5 mV/s) and with 60 % capacitance retention during the high-speed charging-discharging process (100 mV/s).