Redetermination of the standard enthalpy of formation of Lu5Ge3 by high temperature, direct synthesis calorimetry

被引：10

作者：

Meschel, SV

Kleppa, OJ

机构：

[1] University of Chicago, James Franck Institute, Chicago, IL 60637

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 1996年 / 245卷

关键词：

lutetium germanide; thermodynamics; direct synthesis calorimetry; enthalpy of formation;

D O I：

10.1016/S0925-8388(96)02672-2

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The standard enthalpies of formation of LuSi, Lu5Sn3 and Lu5Ge3 have been remeasured by direct synthesis calorimetry at 1473 +/- 2K. The following Delta H-1 degrees (kJ mol(-1)) values of atoms are reported: LuSi -79.1 +/- 2.7; Lu5Sn3 -75.1 +/- 2.7; Lu5Ge3 -93.1 +/- 2.2. The results are compared with our previously reported values.

引用

页码：L28 / L29

页数：2

共 50 条

[1] Redetermination of the standard enthalpy of formation of Lu5Ge3 by high temperature, direct synthesis calorimetry
Meschel, S.V.
Kleppa, O.J.
Journal of Alloys and Compounds, 1996, 245 (1-2):
[2] Heat capacity and enthalpy of Lu5Ge3 in the temperature range 57-2355 K
Gorbachuk, N.P., 2001, Naukova Dumka : 9 - 10
[3] REDETERMINATION OF THE STANDARD ENTHALPIES OF FORMATION OF LAPT, LUPT AND LUPT, BY HIGH-TEMPERATURE DIRECT SYNTHESIS CALORIMETRY
GUO, QT
KLEPPA, OJ
JOURNAL OF ALLOYS AND COMPOUNDS, 1995, 218 (02) : L21 - L23
[4] Heat capacity and enthalpy of Lu5Ge3 at 57-2355 K
Gorbachuk, NP
Bolgar, AS
POWDER METALLURGY AND METAL CERAMICS, 2001, 40 (9-10) : 512 - 515
[5] Heat Capacity and Enthalpy of Lu5Ge3 at 57-2355 K
Nikolai P. Gorbachuk
Powder Metallurgy and Metal Ceramics, 2001, 40 : 512 - 515
[6] Note on the standard enthalpies of formation of LuNi5, Lu3Pd4 and LuPd, determined by high temperature direct synthesis calorimetry
Guo, QT
Kleppa, OJ
JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 256 (1-2) : L15 - L17
[7] Note on the standard enthalpies of formation of LuNi5, Lu3Pd4 and LuPd, determined by high temperature direct synthesis calorimetry
Guo, Qiti
Kleppa, Ole J.
1997, Elsevier Science S.A., Lausanne, Switzerland (256) : 1 - 2
[8] STANDARD ENTHALPIES OF FORMATION OF 5D ALUMINIDES BY HIGH-TEMPERATURE DIRECT SYNTHESIS CALORIMETRY
MESCHEL, SV
KLEPPA, OJ
JOURNAL OF ALLOYS AND COMPOUNDS, 1993, 197 (01) : 75 - 81
[9] Standard enthalpies of formation of 5d aluminides by high-temperature direct synthesis calorimetry
Meschel, S.V., 1600, (197):
[10] Note on the standard enthalpies of formation of Ta5Ge3 and OsGe2 by direct synthesis calorimetry
Meschel, S.V., 1600, Elsevier Science S.A., Lausanne, Switzerland (216):

← 1 2 3 4 5 →