Chemical Composition Influence on Microhardness, Microstructure and Phase Morphology of AlxCrFeCoNi High Entropy Alloys

The AlCrFeCoNi high entropy alloy exhibits unexpected properties that can be obtained after mixing five different elements, which could not be obtained from any one independent element. The difference to conventional alloys is that these alloys may have, at the same time, both hardness and plasticity, can be used in severe impact applications. In order to study the influence of aluminum content on the microhardness and microstructure of the high entropy alloys AlxCrFeCoNi (x: atomic ratio, x= 0.2 to 2.0) nine types of samples were obtained as mini-sized ingots (50x15x9.5 mm and 40 g weight). The mini-ingots were obtained using arc melt casting process in a vacuum arc remelting device (VAR MRF ABJ 900). The influence of the chemical elements on the microstructure, phases morphology and microhardness of AlxCrFeCoNi system was studied. The results have confirmed that mechanical properties could be greatly adjusted by the chemical composition change. The main element that influences the microhardness of the analyzed system is aluminum, due to the formation of Al-Fe compounds with high hardness. Increasing the aluminum content in the alloy to values greater than 1.8... 2 at.% contribute to the increase of hardness and also to the embrittlement thereof. Other elements like Cr, Fe, Co and Ni can contribute to mitigate increasing the hardness of the alloy. The type of phases formed in high entropy alloy are dependent to the aluminum concentration. So, depending on of aluminium content, different phases are obtained, like FCC for low Al content, mixture of FCC and BCC for about 2.5 % Al and BCC for high Al content.