Intercrystalline Corrosion Cracking of the Austenitic Steels for Power Equipment on the Base of Field Experience

被引：0

作者：

Bazaras, Z. ^{[1
]}

Timofeev, B. ^{[1
]}

Vasilieva, N. ^{[1
]}

Fedorova, V. ^{[1
]}

机构：

[1] Kaunas Univ Technol, LT-35212 Panevezys, Lithuania

来源：

MECHANIKA 2013: PROCEEDINGS OF THE 18TH INTERNATIONAL CONFERENCE | 2013年

关键词：

welded joint; pipelines; intercrystalline corrosion cracking; nuclear power plant; sensitization; MECHANICAL STRENGTH; WELDED-JOINTS;

D O I：

暂无

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper questions related to damage of the power equipment from austenitic stainless steel are considered. It is established, that occurrence of cracks type intercrystalline corrosion fracture in the austenitic stainless steel welded joint heat-affected zone caused by 3 factors - the certain degree of base metal sensitization, high operating voltage level and increased (in comparison with the normative documentation at operation) oxygen concentration in the heat-carrying agent.

引用

页码：32 / 37

页数：6

共 50 条

[1] Intercrystalline corrosion cracking of power equipment made of austenitic steels
Timofeev, BT
Fedorova, VA
Buchatskii, AA
[J]. MATERIALS SCIENCE, 2004, 40 (01) : 48 - 59
[2] Intercrystalline Corrosion Cracking of Power Equipment Made of Austenitic Steels (Review)
B. T. Timofeev
V. A. Fedorova
A. A. Buchatskii
[J]. Materials Science, 2004, 40 : 48 - 59
[3] CORROSION CRACKING AND INTERCRYSTALLINE CORROSION OF CHROME-MANGANESE-NICKEL AUSTENITIC STEELS
CHUMALO, GV
MELEKHOV, RK
FEDYAKIN, PN
KOVAL, MV
[J]. SOVIET MATERIALS SCIENCE, 1989, 25 (06): : 607 - 609
[4] THERMODYNAMIC ANALYSIS OF INTERCRYSTALLINE CORROSION OF AUSTENITIC STEELS
BOGOLYUBSKIY, SD
GOLOVANENKO, SA
TOMILIN, IA
ULYANIN, EA
[J]. RUSSIAN METALLURGY, 1976, (03): : 138 - 145
[5] Intercrystalline corrosion cracking of welded joints of the austenitic pipelines of nuclear power plants
Timofeev, BT
Fedorova, VA
Buchatskii, AA
[J]. MATERIALS SCIENCE, 2004, 40 (05) : 676 - 683
[6] Intercrystalline Corrosion Cracking of Welded Joints of the Austenitic Pipelines of Nuclear Power Plants
B. T. Timofeev
V. A. Fedorova
A. A. Buchatskii
[J]. Materials Science, 2004, 40 : 676 - 683
[7] STRESS-CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS IN CHEMICAL PLANT EQUIPMENT
RION, WC
[J]. INDUSTRIAL AND ENGINEERING CHEMISTRY, 1957, 49 (03): : A73 - A78
[8] CAUSTIC CRACKING IN STEAM BOILERS - THE INTERCRYSTALLINE CORROSION OF MILD STEELS
PARKINS, RN
[J]. CHEMISTRY & INDUSTRY, 1953, (09) : 180 - 184
[9] STRESS CORROSION CRACKING OF AUSTENITIC STAINLESS STEELS
HARWOOD, JJ
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1958, 105 (03) : C50 - C50
[10] IMPROVED STRESS EQUIPMENT FOR TESTING OF STEELS FOR INTERCRYSTALLINE STRESS CORROSION CRACKING USING TESTPIECES ACCORDING TO JONES,JA
HUMMITZSCH, W
ZWINTZSC.W
[J]. ARCHIV FUR DAS EISENHUTTENWESEN, 1968, 39 (11): : 849 - +

← 1 2 3 4 5 →