Structure Evolution of 7YSZ Thermal Barrier Coating During Thermal Shock Testing

被引：7
|
作者：
Zhang Xiao-Feng [1 ,2 ,3 ]
Zhou Ke-Song [1 ,2 ,3 ]
Zhang Ji-Fu [2 ,3 ]
Zhang Yong [2 ,3 ]
Liu Min [2 ,3 ]
Deng Chun-Ming [2 ,3 ]
机构：
[1] S China Univ Technol, Sch Mat Sci & Engn, Guangzhou 510640, Guangdong, Peoples R China
[2] Guangzhou Res Inst Nonferrous Met, Natl Engn Lab Modern Mat Surface Engn Technol, Guangzhou 510650, Guangdong, Peoples R China
[3] Guangzhou Res Inst Nonferrous Met, Inst New Mat, Guangzhou 510650, Guangdong, Peoples R China
来源：
JOURNAL OF INORGANIC MATERIALS | 2015年 / 30卷 / 12期
关键词：
thermal shock; TGO; failure mechanism; structure evolution; STRESS-DISTRIBUTION; TGO CREEP; TOP-COAT; FAILURE; MECHANISMS; OXIDATION; BEHAVIOR; DESIGN; SYSTEM; CYCLE;
D O I：
10.15541/jim20150199
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Bond coating NiCoCrAlYTa was prepared on nickel-based superalloy by low temperature-high velocity oxygen flame (LT-HVOF). Then 7wt% Y2O3 stabilized ZrO2 ceramic coating was fabricated on bond coating by air plasma spray (APS). Diffusion principles of bond coating were investigated under thermal cycle by using multi-functional flame tester. Sintering and phase transformation of ceramic coating were studied. The experiment results show that with thermal cycle increase, thermally grown oxide (TGO) forms at the interface of ceramic-bond coating and its thickness continuously increases. Besides, the bond coating further diffuses to surface of ceramic coating. Lots of oxides appears on the surface of ceramic coating nearing microcrack. Diffusion of bond coating to surface contributes to sintering of ceramic coating, which leads to increase of microhardness. Additionally, plenty of voids were appeares in bond coating for Kirkendall effect resulting in decrease of microhardness. Large-scale cracks are observed after thermal cycle due to phase transformation and thermal residual stress.
引用
收藏
页码：1261 / 1266
页数：6
相关论文
共 19 条
  • [1] Ceramic materials for thermal barrier coatings
    Cao, XQ
    Vassen, R
    Stoever, D
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) : 1 - 10
  • [2] Pre-oxidation and TGO growth behaviour of an air-plasma-sprayed thermal barrier coating
    Chen, W. R.
    Wu, X.
    Marple, B. R.
    Lima, R. S.
    Patnaik, P. C.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2008, 202 (16): : 3787 - 3796
  • [3] Materials design for the next generation thermal barrier coatings
    Clarke, DR
    Levi, CG
    [J]. ANNUAL REVIEW OF MATERIALS RESEARCH, 2003, 33 : 383 - 417
  • [4] Mechanisms controlling the durability of thermal barrier coatings
    Evans, AG
    Mumm, DR
    Hutchinson, JW
    Meier, GH
    Pettit, FS
    [J]. PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) : 505 - 553
  • [5] CERAMIC STEEL
    GARVIE, RC
    HANNINK, RH
    PASCOE, RT
    [J]. NATURE, 1975, 258 (5537) : 703 - 704
  • [6] Guan HR, 2002, ACTA METALL SIN, V38, P1133
  • [7] Thermal barrier coatings for enhanced efficiency of gas turbine engines
    Gurrappa, I.
    Rao, A. Sambasiva
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 201 (06): : 3016 - 3029
  • [8] On TGO creep and the initiation of a class of fatigue cracks in thermal barrier coatings
    Hernandez, Mercedes T.
    Karlsson, Anette M.
    Bartsch, Marion
    [J]. SURFACE & COATINGS TECHNOLOGY, 2009, 203 (23): : 3549 - 3558
  • [9] Progress of Research on the Failure Mechanism of Thermal Barrier Coatings
    Hua Jia-Jie
    Zhang Li-Peng
    Liu Zi-Wei
    Wang Yong-Zhe
    Lin Chu-Cheng
    Zeng Yi
    Zheng Xue-Bing
    [J]. JOURNAL OF INORGANIC MATERIALS, 2012, 27 (07) : 680 - 686
  • [10] Isothermal oxidation behavior of cryomilled NiCrAlY bond coat: Homogeneity and growth rate of TGO
    Ma, Kaka
    Schoenung, Julie M.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2011, 205 (21-22): : 5178 - 5185
12