Conductive PEDOT:PSS-Based Organic/Inorganic Flexible Thermoelectric Films and Power Generators

We present a simple thermoelectric device that consists of a conductive poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)-based inorganic/organic thermoelectric film with high thermoelectric performance. The PEDOT:PSS-coated Se NWs were first chemically synthesized in situ, and then mixed with an Ag precursor solution to produce the PEDOT:PSS-coated Ag2Se NWs. The PEDOT:PSS matrix was then treated with dimethyl sulfoxide (DMSO) prior to the production of flexible PEDOT:PSS-coated Ag2Se NW/PEDOT:PSS composite films with various weight fractions of Ag2Se via a simple drop-casting method. The thermoelectric properties (Seebeck coefficient, electrical conductivity, and power factor) of the composite films were then analyzed. The composite film with 50 wt.% NWs exhibited the highest power factor of 327.15 mu W/m center dot K-2 at room temperature. The excellent flexibility of this composite film was verified by bending tests, in which the thermoelectric properties were reduced by only similar to 5.9% after 1000 bending cycles. Finally, a simple thermoelectric device consisting of five strips of the proposed composite film was constructed and was shown to generate a voltage of 7.6 mV when the temperature difference was 20 K. Thus, the present study demonstrates that that the combination of a chalcogenide and a conductive composite film can produce a high-performance flexible thermoelectric composite film.