On the fracture behavior of uranium subjected to shock-wave loading in the temperature range -196 to 800 degrees C

被引：0
|
作者：
Golubev, VK
Sobolev, YS
Yukina, NA
机构：
来源：
RUSSIAN METALLURGY | 1997年 / 02期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The spall-type fracture of uranium was investigated in the temperature range -196 to 800 degrees C. The critical levels of shock-wave loading were determined, responsible for the initiation of the spall sites and complete macroscopic failure of the specimens. The data are described of metallographic research into the fracture behavior of uranium at various test temperatures.
引用
收藏
页码：103 / 105
页数：3
相关论文
共 50 条
  • [1] On the fracture behavior of uranium subjected to shock-wave loading in the temperature range -196 to 800oC
    Golubev, V. K.
    Sobolev, Y. S.
    Yukina, N. A.
    Russian Metallurgy, (02):
  • [2] Failure of uranium alloys with molybdenum and zirconium under shock-wave loading in the temperature range from -196 to 800°C
    Golubev, VK
    Sobolev, YS
    Yukina, NA
    RUSSIAN METALLURGY, 1998, (01): : 130 - 131
  • [3] Type of fracture of the U-Mo and U-Zr alloys under shock-wave loading in the range from -196 to 800°C
    Golubev, V.K.
    Sobolev, Yu.S.
    Yukina, N.A.
    Izvestia Akademii nauk SSSR. Metally, 1998, (01): : 107 - 108
  • [4] MECHANICAL PROPERTIES OF STANDARD AUSTENITIC STAINLESS STEELS IN TEMPERATURE RANGE -196 DEGREES TO +800 DEGREES C
    SANDERSON, GP
    LLEWELLYN, DT
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1969, 207 : 1129 - +
  • [5] Deformation behavior and spall fracture of the Hadfield steel under shock-wave loading
    S. F. Gnyusov
    V. P. Rotshtein
    S. D. Polevin
    S. A. Kitsanov
    Russian Physics Journal, 2011, 53 : 1046 - 1052
  • [6] DEFORMATION BEHAVIOR AND SPALL FRACTURE OF THE HADFIELD STEEL UNDER SHOCK-WAVE LOADING
    Gnyusov, S. F.
    Rotshtein, V. P.
    Polevin, S. D.
    Kitsanov, S. A.
    RUSSIAN PHYSICS JOURNAL, 2011, 53 (10) : 1046 - 1052
  • [7] Compressive fracture of brittle solids under shock-wave loading
    Kanel, GI
    Bless, SJ
    CERAMIC ARMOR MATERIALS BY DESIGN, 2002, 134 : 197 - 216
  • [8] Characterization of adhesively bonded aluminum plates subjected to shock-wave loading
    Yildiz, Salih
    Andreopoulos, Yiannis
    Jensen, Robert E.
    Shaffren, Daniel
    Jahnke, Douglas
    Delale, Feridun
    INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2019, 127 (86-99) : 86 - 99
  • [9] ELECTRICAL RESPONSE OF SHOCK-WAVE COMPRESSED PZT CERAMICS SUBJECTED TO AXIAL SHOCK LOADING
    BAUER, F
    VOLLRATH, K
    EYRAUD, L
    FETIVEAU, Y
    BULLETIN OF THE AMERICAN PHYSICAL SOCIETY, 1979, 24 (04): : 727 - 727
  • [10] THE OXIDATION OF COPPER IN THE TEMPERATURE RANGE 200-DEGREES-C-800-DEGREES-C
    TYLECOTE, RF
    JOURNAL OF THE INSTITUTE OF METALS, 1953, 81 (12): : 681 - &
12345