Modification of Thiol-Ene Ionogels with Octakis(methacryloxypropyl) Silsesquioxane

The effect of polyhedral oligomeric silsesquioxane (POSS) on the synthesis and properties of hybrid organic-inorganic ionogels was investigated using octakis(methacryloxypropyl) silsesquioxane (methacryl-POSS). Ionogels were prepared in situ by thiol-ene photopolymerization of triallyl isocyanurate with pentaerythritol tetrakis(3-mercaptopropionate) in a mixture of imidazolium ionic liquid 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMImNTf(2)) and propylene carbonate (PC). Investigations included the kinetics of hybrid materials formation and selected physical and mechanical properties. The disadvantage of ionogels without the methacryl-POSS modifier is leakage and insufficient mechanical properties. Modifying the thiol-ene matrix by the addition of methacryl-POSS made it possible to obtain non-leaking ionogels with improved mechanical and conductive properties. The steric hindrance of POSS cages and high-density network formation played important roles in ionogel synthesis: decrease of polymerization rate (with almost no effect on conversion), as well as dimensions of the formed polymer spheres during dispersion polymerization (highly cross-linked polymer has poorer solubility in polymerizing medium at a similar conversion, and nucleation begins at lower conversion), an increase of glass transition temperature and puncture strength. Hybrid ionogels with high ionic conductivity in the range of 4.0-5.1 mS center dot cm(-1) with the maximum parameter for 1.5 wt.% addition of the methacryl-POSS were obtained, which can be associated with ion-pair dissociations in ionic liquid clusters caused by methacryl-POSS.