Deformation and fracture behaviors of K403 Ni-based superalloy at elevated temperatures

The effects of the deformation temperatures (850 C-1000 degrees C), the strain rates (0.01 s(-1) to 10 s(-1)) and the stress states on the deformation and fracture behaviors of K403 Ni-based superalloy were investigated by thermal compression and tensile simulating tests using Gleeble-1500 thermo-simulation machine. The microstructure evolution and fracture surface was also investigated using scanning electron microscope and transmission electron microscope, with the aim to elucidate the deformation and fracture mechanism. It was found that increasing the strain rates increases the peak stress and the yield stress, but decreases the elongation and the yield strain. In contrast, increasing the deformation temperatures decreases the peak stress and the yield stress, but increases the elongation and the yield strain. Various dislocation cells were observed after the deformation at 850 degrees C. Increasing the deformation temperatures decreases the dislocation density. Brittle quasi-cleavage fracture morphology was observed at the temperatures below 900 degrees C. Increasing the deformation temperatures changes the fracture from quasi-cleavage fracture to inter-granular fracture. The fracture mechanism of K403 alloy at high temperatures was revealed, and the high temperature fracture model of K403 alloy was established. (C) 2016 Elsevier B.V. All rights reserved.