Immobilization of glucose oxidase on the films prepared by electrochemical copolymerization of pyrrole and 1-(2-carboxyethyl)pyrrole for glucose sensing

Glucose oxidase (GOx) was immobilized through amide linkages on the surfaces of the conducting polymer films prepared by electrochemical copolymerization of pyrrole (Py) and 1-(2-carboxyethyl)pyrrole (Py-COOH) for the purpose of fabricating GOx-immobilized electrodes for amperometric sensing of glucose. The conductivity of the copolymer film was in the range 10(-8)-10(-3) S/cm and showed a tendency to decrease with increasing content of Py-COOH units in the copolymer. The amount of immobilized GOx increased significantly with increasing content of Py-COOH units in the copolymer film up to 30%, and showed a tendency to level off when the content of Py-COOH units became larger. The activity of immobilized GOx per area of the copolymer film decreased slightly with increasing content of Py-COOH units in the copolymer. Although the GOx-immobilized copolymer films gave the amperometric response to glucose depending on its concentration, the magnitude of the response to a given concentration was found to decrease with increasing content of Py-COOH units in the copolymer. The variation in the amperometric response was attributed to the difference in conductivity of the copolymer film. The appropriate content of Py-COOH units in the copolymer was considered to be 5% or less for the amperometric sensing of glucose with the GOx-immobilized copolymer film. (c) 2006 Elsevier Ltd. All rights reserved.