Crystallization kinetics of compatibilized blends of liquid crystalline polymer with PEEK

A fully aromatic thermotropic liquid crystalline polyester (TLCP) has been blended with poly(ether ether ketone) (PEEK). Multiblock copolymer (BCP) was used as the compatibilizer in the concentration at 2 phr. The isothermal crystallization kinetics and morphology of compatibilized blends were studied using differential scanning calorimetry (DSC) and polar light micrograph (PLM). TLCP acted as a heterogenous nucleation sites to accelerate the crystallization for PEEK. However, PEEK crystallization rates decreased with increasing TLCP fraction. Isothermal crystallization exotherms showed that the addition of BCP retarded crystallization of PEEK in PEEK/TLCP blend, which was probably resulted from the constraint effect of BCP as well as the size reduction of PEEK spherulite domain. The equilibrium melting temperature of PEEK for blends was below that of pure PEEK. After adding BCP, it decreased further. Morphological analysis showed that it was difficult to discern the single PEEK spherulites when BCP was added.