Creep of Cast Steel P91 with Weld Joint

被引：0
|
作者：
Vlasak, Tomas [1 ]
Hakl, Jan [1 ]
Novak, Pavel [1 ]
Sochor, Jiri [2 ]
Cech, Jan [2 ]
机构：
[1] SVUM As, Podnikatelska 565, Prague 19011 9, Czech Republic
[2] ZDAS a s, Prague, Czech Republic
来源：
METALLOGRAPHY XV | 2014年 / 782卷
关键词：
creep; cast steel; welding;
D O I：
10.4028/www.scientific.net/MSF.782.331
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High-temperature martensitic steel P91, internationally marked GX12CrMoVNbN91, is the material used in the energy industry. Creep and high-temperature corrosion resistances are important properties that affect the application of this material at higher temperatures. Weldment reduces creep properties of construction. This work deals with the quantification of creep properties decrease in the case of material P91. The main focus is besides the evaluation of creep test results given to the mathematical description of the weld creep strength reduction. In addition metallographic analyses of weld joint after creep exposures were performed.
引用
收藏
页码：331 / +
页数：2
相关论文
共 50 条
  • [1] Microstructural changes in creep exposed P91 steel weld joint
    Jandova, Dagmar
    Kasl, Josef
    MATERIALS AT HIGH TEMPERATURES, 2011, 28 (02) : 137 - 146
  • [2] Creep Crack Growth Behavior of a P91 Steel Weld
    Venugopal, S.
    Sasikala, G.
    Kumar, Yatindra
    STRUCTURAL INTEGRITY, 2014, 86 : 662 - 668
  • [3] CREEP STRENGTH DECREASE OF CAST STEEL P91 WELDMENTS
    Vlasak, Tomas
    Hakl, Jan
    Novak, Pavel
    Sochor, Jiri
    Cech, Jan
    METAL 2013: 22ND INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2013, : 851 - 855
  • [4] Creep cavities and carbide evolution in interrupted creep conditions along P91 steel of dissimilar weld joint
    Awale, Deepshree D.
    Dandekar, Tushar R.
    Ballal, Atul R.
    Thawre, Manjusha M.
    Journal of Adhesion Science and Technology, 2024, 38 (23) : 4190 - 4201
  • [5] Creep cavities and carbide evolution in interrupted creep conditions along P91 steel of dissimilar weld joint
    Awale, Deepshree D.
    Dandekar, Tushar R.
    Ballal, Atul R.
    Thawre, Manjusha M.
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2024,
  • [6] Creep resistance of similar and dissimilar weld joints of P91 steel
    Jandova, Dagmar
    Kasl, Josef
    Kanta, Vaclav
    MATERIALS AT HIGH TEMPERATURES, 2006, 23 (3-4) : 165 - 170
  • [7] Influence of Substructure on Creep Failure of P91 Steel Weld Joints
    Jandova, Dagmar
    Kasl, Josef
    Kanta, Vaclav
    CREEP & FRACTURE IN HIGH TEMPERATURE COMPONENTS: DESIGN & LIFE ASSESSMENT ISSUES, PROCEEDINGS, 2009, : 177 - 188
  • [8] Role of microstructures on heterogeneous creep behaviour across P91 steel weld joint assessed by impression creep testing
    Sakthivel, T.
    Sasikala, G.
    Vasudevan, M.
    MATERIALS CHARACTERIZATION, 2020, 159
  • [9] Influence of precipitation on dislocation substructure and creep properties of P91 steel weld joints
    Jandova, Dagmar
    Kasl, Josef
    MATERIALS AT HIGH TEMPERATURES, 2010, 27 (02) : 135 - 140
  • [10] Study on A Kind of White Massive Microstructure in P91 Steel Weld Joint
    Xu, XueXia
    Feng, YanTing
    Li, WenPeng
    Sun, Peng
    Ouyang, Jie
    Niu, XiaoGuang
    MATERIALS PROCESSING TECHNOLOGY II, PTS 1-4, 2012, 538-541 : 1522 - 1525
12345