Surface Tension and Related Ions Behavior of Silicate Melts of the Na2O-K2O-SiO2-CaF2 System under Ultrasonic Irradiation

被引：6

作者：

Min, Yi ^{[1
,2
,3
]}

Jiao, Shiyan ^{[1
,3
]}

Zhang, Rui ^{[1
,3
]}

Jia, Jixiang ^{[2
]}

Qi, Jie ^{[1
,3
]}

Liu, Chengjun ^{[1
,3
]}

机构：

[1] Minist Educ, Key Lab Ecol Met Multimetall Ores, Shenyang 110819, Liaoning, Peoples R China

[2] State Key Lab Met Mat Marine Equipment & Applicat, Anshan 114021, Liaoning, Peoples R China

[3] Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China

来源：

ISIJ INTERNATIONAL | 2021年 / 61卷 / 03期

基金：

国家重点研发计划; 中国国家自然科学基金;

关键词：

surface tension; melt structure; ion behavior; ultrasonic;

D O I：

10.2355/isijinternational.ISIJINT-2020-557

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Under ultrasonic irradiation, surface tension and structure of molten slags of Na2O-K2O-SiO2-CaF2 system were measured. Results showed that, the slags were degraded gradually with the increase of ultrasonic intensity and silica tetrahedron radicals with oxygen vacancies generated in the melts. In fluorine free slag, the dissociated radicals coordinate with free oxygen anions, which lead to the decrease of electrostatic force between ions and the related decrease of surface tension. While in fluorine bearing slag, the surface tension increases for the reason that the free fluorine anions dominate the behavior of coordination, which lead to the increase of electrostatic force between ions. The increase of surface tension will promote the down flow of mold flux between the gap of solidified steel shell and the mold copper wall, which will facilitate the lubrication between them.

引用

页码：1022 / 1028

页数：7

共 50 条

[1] ULTRASONIC INVESTIGATION OF MELTS IN THE SYSTEM NA2O-AL2O3-SIO2
KRESS, VC
WILLIAMS, Q
CARMICHAEL, ISE
GEOCHIMICA ET COSMOCHIMICA ACTA, 1988, 52 (02) : 283 - 293
[2] Multicomponent diffusion in silicate melts: SiO2-TiO2-Al2O3-MgO-CaO-Na2O-K2O System
Guo, Chenghuan
Zhang, Youxue
GEOCHIMICA ET COSMOCHIMICA ACTA, 2016, 195 : 126 - 141
[3] SURFACE TENSION OF MELTS IN THE SYSTEM CaO-SiO2-15% Al2O3-MgO-CaF2.
Kim, A.S.
Akberdin, A.A.
Kulikov, I.S.
Russian metallurgy. Metally, 1984, (05) : 32 - 35
[4] SURFACE-TENSION OF LI2O-CAF2 MELTS
OVCHARENKO, GI
LEPINSKIKH, BM
BAKUMENKO, SP
ZHURNAL FIZICHESKOI KHIMII, 1976, 50 (04): : 973 - 975
[5] Density and Surface Tension of CaO-SiO2-Al2O3-R2O (R=Li, Na, K) Melts
Sukenaga, Sohei
Haruki, Shinichiro
Nomoto, Yoshitaka
Saito, Noritaka
Nakashima, Kunihiko
ISIJ INTERNATIONAL, 2011, 51 (08) : 1285 - 1289
[6] Thermodynamics of phosphorus in CaO-K2O-CaF2-SiO2 melts
Kimura, H
Tsukihashi, F
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1997, 83 (11): : 689 - 694
[7] Investigation on surface tension of CaF2-CaO-SiO2 (-MgO-Al2O3) melts
Lao, Yigui
Gao, Yunming
Wang, Qiang
Li, Guangqiang
METALLURGICAL RESEARCH & TECHNOLOGY, 2024, 121 (05)
[8] Effect of fluorine on surface tension of CaO-SiO2-Al2O3-Na2O-CaF2 mold flux
Gao, Qiang
Cao, Longhu
METALLURGICAL RESEARCH & TECHNOLOGY, 2021, 118 (03)
[9] Ultrasonic depolymerization of Li2O-Na2O-SiO2 type silicate melt
Min, Yi
Shi, Zhenxing
Liu, Chengjun
ULTRASONICS SONOCHEMISTRY, 2017, 39 : 727 - 732
[10] Surface Tension and Density of Slag Melts of the CaF2-MgO-Al2O3 System with SiO2 Additives.
Povolotskii, D.Ya.
Roshchin, V.E.
Gribanov, V.P.
Verkhorubov, V.V.
Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya, 1982, (12): : 1 - 3

← 1 2 3 4 5 →